POLYARYLENE SULFIDE RESIN COMPOSITION HAVING EXCELLENT CHEMICAL RESISTANCE
The present invention provides a resin composition comprising a polyarylene sulfide, glass fiber, a mercaptosilane compound, and hydrotalcite, the resin composition having a chlorine content of 100 ppm or less and a sodium content of 50 ppm or less. The resin composition is excellent in chemical resistance against organic solvents and antifreeze resistance while maintaining excellent mechanical and thermal properties inherent to PAS, and thus the resin composition can be widely used in various fields requiring excellent chemical resistance and antifreeze resistance.
1 . A resin composition comprising:
a polyarylene sulfide having a chlorine content of 100 ppm or less and a sodium content of 50 ppm or less;
a glass fiber;
a mercaptosilane compound; and
a hydrotalcite.
2 . The resin composition of claim 1 , wherein the polyarylene sulfide comprises 10 to 10,000 ppm of main chain-bound iodine or free iodine.
3 . The resin composition of claim 1 , wherein the polyarylene sulfide has a number average molecular weight of 5,000 to 50,000 and a melt viscosity of 10 to 50,000 poise as measured by a rotating disk viscometer at 300° C.
4 . The resin composition of claim 1 , wherein the glass fiber has an average diameter of 6 to 15 μm and an average length of 2 to 5 mm.
5 . The resin composition of claim 1 , wherein the glass fiber is an alumino-borosilicate glass fiber.
6 . The resin composition of claim 1 , wherein the mercaptosilane compound is a dry silane which is prepared by impregnating a porous inorganic substance with a liquid silane.
7 . The resin composition of claim 1 , wherein the hydrotalcite has an average particle diameter of 0.3 to 0.8 μm.
8 . The resin composition of claim 1 , wherein the resin composition comprises 40 to 70 wt % of the polyarylene sulfide, 20 to 55 wt % of the glass fiber, 0.01 to 1.5 wt % of the mercaptosilane compound, and 0.05 to 5.0 wt % of the hydrotalcite based on the total weight of the resin composition.
9 . The resin composition of claim 1 , wherein:
the polyarylene sulfide comprises 10 to 10,000 ppm of main chain-bound iodine or free iodine;
the glass fiber is an alumino-borosilicate glass fiber; and
the hydrotalcite has an average particle diameter of 0.3 to 0.8 μm.
10 . The resin composition of claim 1 , wherein the resin composition further comprises a component selected from the group consisting of a heat stabilizer, a lubricant, an antistatic agent, a nucleating agent, a slipping agent, a pigment and any combination thereof.
11 . The resin composition of claim 1 , wherein the resin composition has a tensile strength change ratio of less than 10% as measured after immersing an injection-molded specimen in a solution containing ethylene glycol and water in a volume ratio of 1:1 at 150° C. for 3,000 hours.
12 . A molded article prepared by molding the resin composition of claim 1 .
13 . The molded article of claim 12 , wherein the molded article is an automobile part, an electric part, or an electronic part.