System and method for additive metal manufacturing
A system for additive metal manufacturing, including a deposition mechanism, a translation mechanism mounting the deposition mechanism to the working volume, and a stage. A method for additive metal manufacturing including: selectively depositing a material carrier within the working volume; removing an additive from the material carrier; and treating the resultant material.
1. A method for forming a physical object, the method comprising:
based on a virtual part model, within a build volume, using a metallic build material, fabricating a part with a geometry corresponding to the virtual part model; and
after fabricating the part, sintering the part to form the physical object;
wherein:
the metallic build material comprises a volatile solvent;
the metallic build material comprises less than 1% polymeric binder by weight;
fabricating the part comprises, for each layer of a plurality of layers of metallic build material:
based on the virtual part model, depositing the layer of metallic build material within the build volume, wherein the deposited layer retains a deposited geometry;
removing the volatile solvent from the layer; and
based on the virtual part model, after removing the volatile solvent from the layer, selectively machining a portion of the layer within the build volume;
the part defines a first volume before sintering;
the physical object defines a second volume after sintering; and
a difference between the first volume and the second volume is between 5% and 12%.
2. The method of claim 1 , wherein the metallic build material is a binderless metal paste comprising:
metal scaffold particles comprising iron, the metal scaffold particles having a D50 particle size; and
metal infiltrant particles with a D50 particle size of less than 20% of the D50 particle size of the metal scaffold particles, wherein the metal infiltrant particles primarily position in interstitial spaces between the metal scaffold particles.
3. The method of claim 2 , wherein:
the metal scaffold particles have a D50 particle size between 1 μm and 8 μm; and
the metal infiltrant particles have a D50 particle size between 50 nm and 1 μm.
4. The method of claim 1 , wherein a first layer of the plurality is deposited onto a substrate held at a substrate temperature, wherein each layer of the plurality is not locally heated between layer deposition and selective machining.
5. The method of claim 1 , wherein, for each layer of the plurality, the portion of the layer is selectively machined by a tool, the method further comprising maintaining an ambient volume proximal the portion of the layer within an uncooled tool operating temperature range throughout fabricating the part, wherein maintaining the ambient volume within the uncooled tool operating temperature range evaporates the volatile solvent from the layer.
6. The method of claim 1 , wherein the metallic build material is ferrous, the method further comprising: applying an attractive magnetic force to the layer while selectively machining the portion of the layer.
7. The method of claim 1 , wherein a first layer of the plurality is deposited onto a build plate, such that the build plate supports the part; wherein the build plate comprises an adhesive interface layer arranged between the build plate and the layer.
8. The method of claim 7 , wherein sintering the part to form the physical object comprises: removing the build plate with the part from the build volume and inserting the build plate with the part into a furnace.