Method for nano powder loading into micro-capillary mold

1. A method of loading powder into a mold, comprising:

immersing the mold comprising one or more microchannels into a suspension comprising the powder and a surfactant suspended in a dispersant, wherein the powder comprises particles having an average particle size of less than 100 μm, wherein the mold is substantially entirely covered by the suspension;

heating the suspension having the mold immersed therein under a temperature condition suitable to lower the stability of the particles of the powder in the suspension such that the particles settle out of solution and into the one or more microchannels; and

applying an ultrasonic wave to the heated suspension to further settle the particles of the powder into the one or more microchannels thereby filling the one or more microchannels of the mold with the powder to provide a filled mold having the powder disposed in the one or more microchannels, wherein the surfactant is one or more of cetyltrimethylammonium based cationic surfactants, and cetryltrimethylammonium-hydrogenosulphate.

2. The method of claim 1 , wherein the ultrasonic wave has a vibration frequency in a range of 5 KHz to 5 MHz.

3. The method of claim 1 , wherein the suspension is heated to a temperature of about 50° C. to about 150° C.

4. The method of claim 1 , wherein the one or more microchannels has a width or diameter of about 1 μm to about 50 μm.

5. The method of claim 1 , wherein the one or more microchannels has a length of about 10 μm to about 50 cm.

6. The method of claim 1 , wherein the dispersant is one or more of water, methanol, ethanol, n-propanol, iso-propanol, N-butanol, ethylene glycol, acetone, acetyl acetone, cyclohexane, ethyl alcohol, glacial acetic acid, dichloromethane, methyl ethyl ketone, and toluene.

7. The method of claim 5 , further comprising removing the mold and decanting the mold.

8. The method of claim 1 , further comprising removing the filled mold from the suspension and drying the filled mold.

9. The method of claim 8 , wherein the mold is dried at a temperature of about 50° C. to about 150° C.

10. The method of claim 1 , further comprising removing the filled mold from the suspension after applying the ultrasonic wave and sintering the filled mold having the powder loaded in the one or more microchannels to thereby form a shaped product.

11. A method for forming a shaped product, comprising:

immersing a mold comprising one or more microchannels into a suspension comprising the powder and a surfactant suspended in a dispersant, wherein the powder comprises particles having an average particle size of less than 100 μm, wherein the mold is substantially entirely covered by the suspension;

heating the suspension having the mold immersed therein under a temperature condition suitable to lower the stability of the particles of the powder in the suspension such that the particles settle out of solution and into the one or more microchannels;

applying an ultrasonic wave to the heated suspension to further settle the particles of the powder into the one or more microchannels thereby filling the one or more microchannels of the mold with the powder; and

removing the mold from the suspension after applying the ultrasonic wave and sintering the mold having the powder loaded in the one or more microchannels to thereby form the shaped product,

wherein the mold is sintered at a temperature of about 1000° C. to about 1800° C.

12. The method of claim 1 , wherein at least a portion of the particles of the powder are non-spherical.

13. The method of claim 1 , wherein the suspension is a colloidal suspension.

14. The method of claim 1 , wherein the powder is present in the suspension in an amount of about 10% to about 40% by weight, based on the total weight of the suspension.

15. A method of loading powder into a mold, comprising:

immersing the mold comprising one or more microchannels into a suspension comprising the powder and a surfactant suspended in a dispersant, wherein the powder comprises particles having an average particle size of less than 100 μm, wherein the mold is substantially entirely covered by the suspension;

heating the suspension having the mold immersed therein under a temperature condition suitable to lower the stability of the particles of the powder in the suspension such that the particles settle out of solution and into the one or more microchannels; and

applying an ultrasonic wave to the heated suspension to further settle the particles of the powder into the one or more microchannels thereby filling the one or more microchannels of the mold with the powder to provide a filled mold having the powder disposed in the one or more microchannels, wherein the powder comprises actinide.

16. The method of claim 1 , wherein the powder comprises metallic particles.

17. The method of claim 1 , wherein the heat and ultrasonic wave are applied simultaneously.

18. The method of claim 1 , wherein the ultrasonic wave is applied after the suspension reaches a temperature of about 70° C. to about 150° C., and heating is maintained during application of the ultrasonic wave.

19. A method of loading powder into a mold, comprising:

immersing the mold comprising one or more microchannels into a suspension comprising the powder and a surfactant suspended in a dispersant, wherein the powder comprises particles having an average particle size of less than 100 μm, wherein the mold is substantially entirely covered by the suspension;

heating the suspension having the mold immersed therein under a temperature condition suitable to lower the stability of the particles of the powder in the suspension such that the particles settle out of solution and into the one or more microchannels; and

applying an ultrasonic wave to the heated suspension to further settle the particles of the powder into the one or more microchannels thereby filling the one or more microchannels of the mold with the powder, wherein the mold is made from a UV curable polymer.