Surfacing materials and method of manufacture

1. A texture-imparting surfacing material, comprising:

a substrate including a top side and a bottom side; and

a matte surface formed on the bottom side thereof, wherein the matte surface of the surfacing material is a coating of an electron beam radiation curable material applied to the bottom side of the substrate, the coating being an epoxy acrylic or urethane acrylic applied to the substrate, wherein the epoxy acrylic or urethane acrylic is irradiated with UV-radiation to produce a UV-irradiated layer wherein the epoxy acrylic or urethane acrylic is only crosslinked on the surface thereof, which produces a matting surface through the effects of a micro-convolution, and is subsequently subjected to electron beam irradiation to crosslink and harden the entire layer and thermal curing to complete curing of the coating due to the inclusion of a peroxide.

2. The texture-imparting surfacing material according to claim 1 , wherein the peroxide is test-butyl peroxybenzoate (TBPB).

3. The texture-imparting surfacing material according to claim 1 , wherein the epoxy acrylic or urethane acrylic is applied to the substrate with a layer thickness of no more than 150 microns.

4. The texture-imparting surfacing material according to claim 3 , wherein the epoxy acrylic or urethane acrylic is applied to the substrate with the layer thickness in a range between 30 and 100 microns.

5. The texture-imparting surfacing material according to claim 1 , wherein the substrate is a plastic, metal, or paper film material.

6. The texture-imparting surfacing material according to claim 5 , wherein the plastic film material is a polypropylene film.

7. A laminate lay-up, comprising:

a texture-imparting release sheet composed of

a release sheet substrate including a top side and a bottom side; and

a matte surface formed on the bottom side thereof, wherein the matte surface of the surfacing material is a coating of an electron beam radiation curable material applied to the bottom side of the release sheet substrate, the coating being an epoxy acrylic or urethane acrylic applied to the release sheet substrate, wherein the epoxy acrylic or urethane acrylic is irradiated with UV-radiation to produce a UV-irradiated layer wherein the epoxy acrylic or urethane acrylic is only crosslinked on the surface thereof, which produces a matting surface through the effects of a micro-convolution, and is subsequently subjected to electron beam irradiation to crosslink and harden the entire layer and thermal curing to complete curing of the coating; and

a decorative laminate, the decorative laminate including,

a decorative layer substrate including a top side and a bottom side; and

a coating formed on the top side thereof, which is placed into contact with the matte surface of the texture-imparting release sheet, the coating being a UV and thermal curable epoxy acrylic or urethane acrylic applied to the top side of the decorative layer substrate,

wherein the coating is applied to the substrate and partially cured via UV-radiation to create a UV-irradiated layer, which is subsequently and fully cured via thermal curing;

a core layer adjacent the bottom side of the decorative layer substrate composed of one or more sheets of paper impregnated with resin,

wherein the thermal curing of the coating of the texture imparting release sheet and the coating of the decorative laminate is effectuated when the laminate lay-up is heated and pressed and is due to the inclusion of a peroxide.

8. The laminate lay-up according to claim 7 , wherein the peroxide is tert-butyl peroxybenzoate (TBPB).

9. The laminate lay-up according to claim 7 , wherein the epoxy acrylic or urethane acrylic of the release sheet and/or the decorative laminate is/are applied with a layer thickness of no more than 150 microns.

10. The laminate lay-up according to claim 9 , wherein the layer thickness of the epoxy acrylic or urethane acrylic of the release sheet is in a range between 30 and 100 microns and the layer thickness of the epoxy acrylic or urethane acrylic of the decorative laminate is in a range between 60 and 80 microns.

11. The laminate lay-up according to claim 7 , wherein the release sheet substrate is a plastic, metal, or paper film material.

12. The laminate lay-up according to claim 11 , wherein the plastic film material is a propylene film.

13. The laminate lay-up according to claim 7 , wherein the decorative layer substrate is a resin impregnated decorative paper.

14. The laminate lay-up according to claim 13 , wherein the decorative laminate further comprises a resin impregnated transparent overlay paper layer between the coating and the top side of the decorative layer substrate.

15. The laminate lay-up according to claim 14 , wherein the overlay is initially B-stage cured and is fully cured when the laminate lay-up is heated and pressed.

16. The laminate lay-up according to claim 13 , wherein the impregnated resin of the decorative layer substrate is a melamine-formaldehyde.

17. The laminate lay-up according to claim 14 , wherein the impregnated resin of the overlay paper layer is a melamine-formaldehyde.

18. The laminate lay-up according to claim 7 , wherein the impregnated resin of the core is a phenolic resin.