Composite particles, method for producing composite particles, and use thereof
In a method for producing composite particles containing polymer particles and silica particles that adhere to the polymer particles, the composite particles are obtained by subjecting a polymerizable monomer to aqueous suspension polymerization in a presence of silica particles and a cellulose compound adsorbing onto the silica particles. The composite particles contain the polymer particles, the silica particles that adhere to surfaces of the polymer particles, and the water-soluble cellulose compound.
1. A method for producing composite particles containing polymer particles and silica particles that adhere to the polymer particles, comprising:
an adsorption step of treating silica particles with a water-soluble cellulose compound by making silica particles coexist with the water-soluble cellulose compound at a temperature of (T-15) ° C. or more, wherein T represents a lower critical solution temperature (° C.) or a cloud point (° C.) of the water-soluble cellulose compound, so as to adsorb the water-soluble cellulose compound onto the surfaces of the silica particles; and
a polymerization step of subjecting a polymerizable monomer to aqueous suspension polymerization in the presence of the silica particles and the water-soluble cellulose compound adsorbing onto surfaces of the silica particles so as to obtain composite particles in which the polymer particles are at least partially covered by a layer of the silica particles.
2. The method for producing composite particles according to claim 1 ,
wherein at least one of hydroxypropyl cellulose and hydroxypropyl methylcellulose is used as the water-soluble cellulose compound.
3. The method for producing composite particles according to claim 1 ,
wherein an amount of the silica particles is from 0.022 to 0.15 g/m 2 per unit surface area of the composite particles.