Nanocomposite membranes and methods of forming the same
A nanocomposite including a mesoporous, macroporous, or a combination thereof oxide and a zeolitic imidazolate framework (ZIF) that is filling the pores of the oxide to form a ZIF phase embedded and at least substantially confined mostly within the oxide. Methods of making nanocomposites including the steps of depositing an oxide in the pores of a mesoporous oxide; and further treating the resulting material with vapor, liquid, or supercritical CO 2 comprising an azole-based compound, a carboxylate based compound, or a combination thereof. Use of disclosed articles to separate propylene and propane in a mixture thereof.
1. A method for fabricating a nanocomposite comprising the steps of:
depositing an oxide in the pores of a mesoporous oxide; and
further treating the resulting material with vapor, liquid, or supercritical CO 2 comprising an azole-based compound, a carboxylate based compound, or a combination thereof.
2. The method of claim 1 , wherein the oxide is deposited using atomic layer deposition (ALD).
3. The method of claim 2 , where the oxide deposited comprises Zn, Co, Fe, In, Cu, Mn, Li, B, Cd, Hg, Pr, Mg, Ni, Al, Zr, Si, Hf, Ti and Ta oxides or a mixture thereof.
4. The method of claim 1 , where the azole based compound comprises any of imidazole, methyl-imidazole, benzimidazole, nitroimidazole, 2-chloro-1H-imidazole, dichloroimidazole, imidazole-2-carboxylic acid, 5,6-dimethylbenzimidazole, imidazole-2-carboxaldehyde, 2-ethylimidazole, 4-bromoimidazolate, 4,5-dichloroimidazolate, dimethylimidazolate or a mixture thereof.
5. The method of claim 1 , where the resulting material is treated with vapor comprising an azole-based compound, a carboxylate based compound, or a combination thereof.