Conductive cellulose nanocrystals, method of producing same and uses thereof
The present disclosure provides a core-shell nanocomposite material comprising an intrinsically conductive polymer (ICP) and surface-modified cellulose nanocrystals (CNCs) as well as synthesis for preparing same and its use thereof in various applications.
1. A process for preparing a composite having a core-shell arrangement, said composite comprising cellulose nanocrystal (CNC) as the core, a first layer comprising at least one surface agent in contact with said CNC and a second layer comprising at least one intrinsically conductive polymer (ICP) in contact with said surface agent; said process comprising:
dispersing the cellulose nanocrystal (CNC) in a solution, wherein said CNC has a rod-like shape with a mean diameter of 10-20 nm and length of 200-400 nm;
mixing the CNC solution and at least one surface agent to cause adsorption of said surface agent on the CNC surface and form said first layer;
adding at least one monomer of said intrinsically conductive polymer (ICP) and polymerizing said monomer at about neutral pH to form said second layer in contact with said first layer comprising the surface agent, wherein said core is individually coated by said ICP; and
isolating said composite.
2. The process of claim 1 , wherein said surface agent is poly(4-vinylpyridine) (P 4 VP), poly(N,N-dimethyl acrylamide) (PDMA), Polyethylenimine (PEI), or poly(N-vinylpyrrolidone) (PVP).
3. The process of claim 1 , wherein said ICP is polypyrrole, polyaniline, polyindole, polythiophene, poly(3-methylthiophene), poly(N-methyl aniline), or poly (o-toluidine).
4. The process of claim 1 , wherein a mass ratio of the surface agent/CNC can range from 5/100 to 100/100.
5. The process of claim 1 , wherein said surface agent is an amphiphilic agent.