Method for continuously manufacturing an aerogel powder having a hydrophobic-hydrophilic bipolar core-shell structure

1. A method for manufacturing an aerogel powder, comprising:

mixing a hydrophilic alkoxysilane compound, a hydrophobic alkyl-substituted alkoxysilane compound, and an organic solvent to form a mixture;

adding an acidic catalyst to the mixture to perform hydrolysis;

adding a basic catalyst to the hydrolyzed mixture to perform condensation, and during the condensation adding a dispersion solvent to the hydrolyzed mixture and stirring the hydrolyzed mixture for gelation so as to form an aerogel granule; and

heating the aerogel granule in a fluidized bed or an oven under a temperature of 80-250° C. to form an aerogel powder;

wherein provided that the dispersion solvent is a hydrophobic dispersion solvent, the aerogel granule is an aerogel granule having a hydrophobic outer shell and a hydrophilic inner core and the aerogel powder is an aerogel powder having a hydrophobic outer shell and a hydrophilic inner core; before completion of the condensation, the hydrolyzed mixture becomes a viscous sol, the hydrophobic dispersion solvent is added to the hydrolyzed mixture, and then the hydrolyzed mixture is stirred so that the hydrolyzed mixture gelates under dispersion force caused by the hydrophobic dispersion solvent to form the aerogel granule having a hydrophobic outer shell and a hydrophilic inner core; or

wherein provided that the dispersion solvent is a hydrophilic dispersion solvent, the aerogel granule is an aerogel granule having a hydrophilic outer shell and a hydrophobic inner core and the aerogel powder is an aerogel powder having a hydrophilic outer shell and a hydrophobic inner core; before completion of the condensation, the hydrolyzed mixture becomes a viscous sol, the hydrophilic dispersion solvent is added to the hydrolyzed mixture, and then the hydrolyzed mixture is stirred so that the hydrolyzed mixture gelates under dispersion force caused by the hydrophilic dispersion solvent to form the aerogel granule is an aerogel granule having a hydrophilic outer shell and a hydrophobic inner core.

2. The manufacturing method as claimed in claim 1 , wherein the hydrophilic alkoxysilane compound is tetramethoxysilane, tetraethoxysilane, R group-trimethoxysilane, or R group-triethoxysilane; each R group is a hydrophilic group comprising a carboxyl group, an amino group, an imino group, a hydroxyl group, an amido group, an epoxy group, or an uricyl group and has 1-8 carbon atom(s).

3. The manufacturing method as claimed in claim 1 , wherein the hydrophobic alkyl-substituted alkoxysilane compound is methyltrimethoxysilane, R′ group-trimethoxysilane, R′ group-tetraethoxysilane, or R′ group-silicone; each R′ group is a hydrophobic group comprising an alky group, an alkenyl group, an ester group, an ether group, an aromatic group, or a halogen and has 1-13 carbon atom(s).

4. The manufacturing method as claimed in claim 1 , wherein the hydrophilic dispersion solvent is water, alcohol, amine, acid, ketone, or ether.

5. The manufacturing method as claimed in claim 1 , wherein the hydrophobic dispersion solvent is ketone, ether, ester, aromatic hydrocarbon, or alkane.

6. The manufacturing method as claimed in claim 1 , wherein based on total moles of the mixture, total content of the hydrophilic alkoxysilane compound and the hydrophobic alkyl-substituted alkoxysilane compound is of 1 mol %-60 mol %, and content of the organic solvent is of 40 mol %-99 mol %.

7. The manufacturing method as claimed in claim 1 , wherein an entity of the hydrophilic alkoxysilane compound and the hydrophobic alkyl-substituted alkoxysilane compound and the acidic catalyst are at a mole ratio of 1:0.5-1:0.00001.

8. The manufacturing method as claimed in claim 1 , wherein the basic catalyst and the acidic catalyst are at a mole ratio of 1:1-5:1.

9. The manufacturing method as claimed in claim 1 , wherein the hydrophilic alkoxysilane compound is tetramethoxysilane or tetraethoxysilane, and the hydrophobic alkyl-substituted alkoxysilane compound is methyltrimethoxysilane.

10. The manufacturing method as claimed in claim 1 , wherein an entity of the hydrophilic alkoxysilane compound and the hydrophobic alkyl-substituted alkoxysilane compound and the acidic catalyst are at a mole ratio of 1:0.5-1:0.00001, and the basic catalyst and the acidic catalyst are at a mole ratio of 1:1-5:1.