Method for producing molten Al plated steel wire
A method of producing an Al plated steel wire comprises a first step of continuously immersing a material steel wire formed of a steel core into a molten Al plating bath and then withdrawing the material steel wire to a gas phase space. The material steel wire plated with a plating metal is brought into contact with a contact member at the plating bath rising portion to produce the Al plated steel wire, the Al plated steel wire having an average diameter D A (mm) and a minimum diameter D MIN (mm) in the longitudinal direction of the wire satisfying the following expression (1) ( D A −D MIN )/ D A ≤0.10, (1). The Al plated steel wire is then wound.
1. A method of producing an Al plated steel wire comprises:
a step of continuously immersing a material steel wire formed of a steel core into a molten Al plating bath and then withdrawing the material steel wire to a gas phase space;
a step of bringing the material steel wire plated with a plating metal into contact with a contact member at the plating bath rising portion to produce the Al plated steel wire, the Al plated steel wire having an average diameter D A (mm) and a minimum diameter D MIN (mm) in the longitudinal direction of the Al plated steel wire satisfying the following expression (1)
( D A −D MIN )/ D A ≤0.10 (1);
and
a step of winding the Al plated steel wire.
2. The method of producing a molten Al plated steel wire according to claim 1 , wherein the material steel wire has a diameter of from 0.05 to 0.50 mm.
3. The method of producing a molten Al plated steel wire according to claim 2 , wherein the material steel wire has on the surface thereof a Zn plated layer or an Ni plated layer having an average thickness of 5 μm or less.
4. The method of producing a molten Al plated steel wire according to claim 1 , wherein the material steel wire has on the surface thereof a Zn plated layer or an Ni plated layer having an average thickness of 5 μm or less.