Stainless steel material for diffusion bonding jig
Provided is a stainless steel material for a diffusion bonding jig in which deformation of bonding members is suppressed while maintaining diffusion bonding properties of the bonding members, and in which releasability (detachability of a bonding member from a release member) after diffusion bonding treatment is excellent. An embodiment of the present invention provides a stainless steel material for a diffusion bonding jig having excellent deformation suppressibility and releasability, the material being a stainless steel material including 1.5 mass % or more of Si, and a ratio (Fr/Fp) of the high-temperature strength (Fr) of the stainless steel material at 1000° C. to the high-temperature strength (Fp) of a bonding member at 1000° C. being 0.9 or more, the bonding member to be bonded by diffusion bonding. The stainless steel material preferably includes C: 0.1 mass % or less, Si: 1.5 to 5.0 mass %, Mn: 2.5 mass % or less, P: 0.06 mass % or less, S: 0.02 mass % or less, Ni: 8.0 to 15.0 mass %, Cr: 13.0 to 23.0 mass %, and N: 0.2 mass % or less.
1. A diffusion bonding jig comprising a stainless steel release member including 1.5 mass % or more of Si, the stainless steel release member being configured to be placed on a bonding member during diffusion bonding,
wherein the bonding member is composed of a plurality of laminated stainless steel places,
wherein a ratio (Fr/Fp) of high-temperature strength (Fr) of the release member at 1000° C. to high-temperature strength (Fp) of the bonding member at 1000° C. being 0.9 or more, and
wherein stainless steel of the stainless steel release member includes C: 0.1 mass % or less, Si: 1.5 to 5.0 mass %, Mn: 2.5 mass % or less, P: 0.06 mass % or less, S: 0.02 mass % or less, Ni: 8.0 to 15.0 mass %, Cr: 13.0 to 23.0 mass %, N: 0.2 mass % or less, and Fe, and unavoidable impurities as a reminder.
2. The diffusion bonding according to claim 1 , wherein the stainless steel further includes one or more selected from the group consisting of Mo: 3.0 mass % or less, Cu: 4.0 mass % or less, Nb: 0.8 mass % or less, Ti: 0.5 mass % or less, V: 1.0 mass % or less, and B: 0.02 mass % or less.
3. The diffusion bonding jig according to claim 1 , wherein the stainless steel further includes one or more selected from the group consisting of Al: 0.2 mass % or less, REM: 0.2 mass % or less, Y: 0.2 mass % or less, Ca: 0.1 mass % or less, and Mg: 0.1 mass % or less.
4. The diffusion bonding jig according to claim 2 , wherein the stainless steel further includes one or more selected from the group consisting of Al: 0.2 mass % or less, REM: 0.2 mass % or less, Y: 0.2 mass % or less, Ca: 0.1 mass % or less, and Mg: 0.1 mass % or less.