Method for incorporating ultraviolet radiation protection and antimicrobial protection into rayon
A method for incorporating ultraviolet radiation protection and antimicrobial protection into rayon is disclosed which has the steps of providing pulp to form cellulose sheets, steeping the cellulose sheets, pressing the cellulose sheets, shredding the cellulose sheets into white crumb, aging the white crumb to form yellow crumb, xanthation of the yellow crumb, dissolving the yellow crumb to form a viscose, adding an additive to the viscose, ripening the viscose, filtering the viscose, degassing the viscose, spinning the viscose to form a fine filament of rayon, drawing the rayon, washing the rayon, and cutting the rayon.
1. A method for incorporating ultraviolet radiation protection and antimicrobial protection into rayon, the method comprising the steps of:
providing pulp to form cellulose sheets;
steeping the cellulose sheets;
pressing the cellulose sheets;
shredding the cellulose sheets into white crumb;
aging the white crumb to form yellow crumb;
xanthation of the yellow crumb;
dissolving the yellow crumb to form a viscose; preparing an additive, which comprises a quantity of prepared zinc oxide particles modified with a layer of a reactive group that forms a bond with the quantity of rayon with the quantity of prepared zinc oxide particles, by suspending a quantity of zinc oxide particles in a solution of 98% ethyl alcohol, suspending a quantity of benzophenone silane linker in the solution of zinc oxide particles and 98% ethyl alcohol, adjusting the pH of the solution of zinc oxide particles, 98% ethyl alcohol and benzophenone silane linker to a pH of 12, placing the pH adjusted solution of zinc oxide particles, 98% ethyl alcohol and benzophenone silane linker into a centrifuge, recovering the centrifuged prepared zinc oxide particles after a period of time and drying the recovered prepared zinc oxide particle for a period of time;
adding said additive to the viscose;
ripening the viscose;
filtering the viscose;
degassing the viscose;
spinning the viscose to form a filament of rayon;
drawing the rayon;
washing the rayon; and
cutting the rayon.
2. The method of claim 1 wherein the time that the recovered prepared zinc oxide particles are dried is eight hours.
3. The method of claim 1 wherein the prepared zinc oxide particles are further coated with titanium.
4. The method of claim 1 wherein the quantity of prepared zinc oxide particles and the quantity of the reactive group are packaged together in a package.
5. The method of claim 1 wherein the viscose has a weight and the zinc oxide particles may be 1-2% based on the weight of the viscose.
6. The method of claim 1 wherein the quantity of prepared zinc oxide particles is five grams.
7. A method for incorporating ultraviolet radiation protection and antimicrobial protection into rayon, the method comprising the steps of:
providing pulp to form cellulose sheets;
steeping the cellulose sheets;
pressing the cellulose sheets;
shredding the cellulose sheets into white crumb;
aging the white crumb to form yellow crumb;
xanthation of the yellow crumb;
dissolving the yellow crumb to form a viscose;
homogenizing the viscose;
adding an additive to the viscose, wherein the additive comprises a quantity of zinc oxide particles and a quantity of a phosphoether of 4-hydroxybenzophenone;
ripening the viscose;
filtering the viscose;
degassing the viscose;
spinning the viscose to form a filament of rayon;
drawing the rayon;
washing the rayon; and
cutting the rayon.
8. The method of claim 7 wherein the quantity of zinc oxide particles is five grams.
9. The method of claim 7 wherein the quantity of zinc oxide particles and the quantity of phosphoether of 4-hydroxybenzophenone are packaged together in a package.
10. The method of claim 7 wherein the viscose has a weight and the zinc oxide particles may be 1-2% based on the weight of the viscose.
11. The method of claim 7 wherein the zinc oxide particles are sized to be small enough to be able to pass through a filter utilized in the filtering step.
12. A method for incorporating ultraviolet radiation protection and antimicrobial protection into rayon, the method comprising the steps of:
providing pulp to form cellulose sheets;
steeping the cellulose sheets;
pressing the cellulose sheets;
shredding the cellulose sheets into white crumb;
aging the white crumb to form yellow crumb;
xanthation of the yellow crumb;
dissolving the yellow crumb to form a viscose; preparing an additive, which comprises a quantity of prepared zinc oxide particles modified with a layer of a reactive group that forms a bond with the quantity of rayon with the quantity of prepared zinc oxide particles, by suspending a quantity of zinc oxide particles in a solution of 98% ethyl alcohol, suspending a quantity of benzophenone silane linker in the solution of zinc oxide particles and 98% ethyl alcohol, adjusting the pH of the solution of zinc oxide particles, 98% ethyl alcohol and benzophenone silane linker to a pH of 12, placing the pH adjusted solution of zinc oxide particles, 98% ethyl alcohol and benzophenone silane linker into a centrifuge, recovering the centrifuged prepared zinc oxide particles after a period of time and drying the recovered prepared zinc oxide particle for a period of time;
adding said additive to the viscose;
homogenizing the viscose;
ripening the viscose;
filtering the viscose;
degassing the viscose;
spinning the viscose to form a filament of rayon;
drawing the rayon;
washing the rayon; and
cutting the rayon.
13. The method of claim 12 wherein the quantity of prepared zinc oxide particles is five grams.
14. The method of claim 12 wherein the time that the recovered prepared zinc oxide particles are dried is eight hours.
15. The method of claim 12 wherein the recovered prepared zinc oxide particles are dried in an oven.
16. The method of claim 12 wherein the quantity of benzophenone silane linker is two grams.