Lightweight, reduced density fire rated gypsum panels
A reduced weight, reduced density gypsum panel that includes high expansion vermiculite with fire resistance capabilities that are at least comparable to (if not better than) commercial fire rated gypsum panels with a much greater gypsum content, weight and density.
1. A gypsum panel comprising:
a gypsum core disposed between cover sheets;
the gypsum core comprising a crystalline matrix of set gypsum and high expansion particles, said particles having a volume expansion of about 300% or more of their original volume after being heated for about one hour at about 1560° F. (850° C.);
the core effective to provide a density of the panel of about 37 pounds per cubic foot (590 kg/m3) or less and a core hardness of at least about 11 pounds (50 N); and,
when the panel is arranged in an assembly constructed in accordance with any one of UL Design Numbers U305, U419 or U423 and having a single layer of the gypsum panel on a first side of the assembly and a single layer of the gypsum panel on a second side of the assembly,
when surfaces of the gypsum panel on the first side of the assembly are heated at temperatures in accordance with the time-temperature curve of ASTM E119-09a,
and when surfaces of the gypsum panels on the second side of the assembly are provided with temperature sensors that provide temperature values pursuant to ASTM E119-09a,
the maximum single value of the temperature sensors is less than about 500° F. (260° C.) after about 50 minutes;
or
the average value of the temperature sensors is less than about 380° F. (190° C.) after about 50 minutes.
2. The gypsum panel according to claim 1 , wherein when the surfaces of gypsum panels on the first side of the assembly are heated:
the maximum single value of the temperature sensors is less than about 500° F. (260° C.) after about 55 minutes; or
the average value of the temperature sensors is less than about 380° F. (190° C.) after about 55 minutes.
3. The gypsum panel according to claim 1 , wherein when the surfaces of gypsum panels on the first side of the assembly are heated:
the maximum single value of the temperature sensors is less than about 500° F. (260° C.) after about 60 minutes; or
the average value of the temperature sensors is less than about 380° F. (190° C.) after about 60 minutes.
4. The gypsum panel according to claim 1 , wherein when the surfaces of gypsum panels on the first side of the assembly are heated:
the maximum single value of the temperature sensors is less than about 500° F. (260° C.) after about 50 minutes; and
the average value of the temperature sensors is less than about 380° F. (190° C.) after about 50 minutes.
5. The gypsum panel according to claim 1 , wherein when the surfaces of gypsum panels on the first side of the assembly are heated:
the maximum single value of the temperature sensors is less than about 500° F. (260° C.) after about 55 minutes; and
the average value of the temperature sensors is less than about 380° F. (190° C.) after about 55 minutes.
6. The gypsum panel according to claim 1 , wherein when the surfaces of gypsum panels on the first side of the assembly are heated:
the maximum single value of the temperature sensors is less than about 500° F. (260° C.) after about 50 minutes; and
the average value of the temperature sensors is less than about 380° F. (190° C.) after about 50 minutes.
7. The gypsum panel of claim 1 , wherein the high expansion particles are high expansion vermiculite particles.
8. The gypsum panel of claim 1 , wherein the panel has a nominal thickness of about ⅝ of an inch (about 16 mm).
9. The gypsum panel of claim 1 , wherein the gypsum panels are effective to inhibit the transmission of heat through the assembly when constructed in accordance with UL Design Number U305 so as to achieve a one hour fire rating under ASTM E119-09a.
10. The gypsum panel of claim 1 , wherein the panel on the first side of the assembly and the panel on the second side of the assembly define an interior cavity of the assembly between the panels, and wherein the interior cavity contains an insulation material selected from mineral wool and fiber glass.
11. The gypsum panel of claim 1 , wherein the gypsum panels are effective to inhibit the transmission of heat through the assembly when constructed in accordance with UL Design Number U419 so as to achieve a one hour fire rating under ASTM E119-09a.
12. The gypsum panel of claim 10 , wherein the gypsum panels are effective to inhibit the transmission of heat through the assembly when constructed in accordance with UL Design Number U423 so as to achieve a one hour fire rating under ASTM E119-09a.
13. The gypsum panel of claim 1 , wherein at least about 50% of the high expansion particles have an average diameter greater than about 300 micrometers.
14. The gypsum panel of claim 1 , wherein at least about 50% of the high expansion particles have an average diameter greater than about 500 micrometers.
15. The gypsum panel of claim 1 , wherein at least one of the cover sheets has a basis weight of about 55 lb/msf to about 65 lb/msf.
16. The gypsum panel of claim 1 , wherein the panel on the first side of the assembly and the panel on the second side of the assembly define an interior cavity of the assembly between the panels, and for at least one of the panels of the assembly the cover sheet facing the interior cavity has a basis weight of about 55 lb/msf to about 65 lb/msf.
17. A gypsum panel comprising:
a gypsum core formed from a mixture comprising:
stucco in an amount of about 1162 to about 1565 lbs/msf (about 5.7 to about 7.6 kg/m2), and
high expansion particles in an amount of up to about 10% by weight of stucco, said particles having a volume expansion of about 300% or more of their original volume after being heated for about one hour at about 1560° F. (850° C.);
the gypsum core disposed between cover sheets;
the core effective to provide a density of the panel of about 37 pounds per cubic foot (590 kg/m3) or less; and
when the panel is arranged in an assembly constructed in accordance with any one of UL Design Numbers U305, U419 or U423 and having a single layer of the gypsum panel on a first side of the assembly and a single layer of the gypsum panel on a second side of the assembly,
when surfaces of the gypsum panel on the first side of the assembly are heated at temperatures in accordance with the time-temperature curve of ASTM E119-09a,
and when surfaces of the gypsum panels on the second side of the assembly are provided with temperature sensors that provide temperature values pursuant to ASTM E119-09a,
the maximum single value of the temperature sensors is less than about 500° F. (260° C.) after about 50 minutes;
or
the average value of the temperature sensors is less than about 380° F. (190° C.) after about 50 minutes.
18. The gypsum panel of claim 17 , wherein the gypsum panels are effective to inhibit the transmission of heat through the assembly when constructed in accordance with UL Design Number U305 so as to achieve a 50 minute fire rating under ASTM E119-09a.
19. The gypsum panel of claim 17 , wherein the gypsum panels are effective to inhibit the transmission of heat through the assembly when constructed in accordance with UL Design Number U305 so as to achieve a one hour fire rating under ASTM E119-09a.
20. The gypsum panel of claim 17 , wherein the gypsum panels are effective to inhibit the transmission of heat through the assembly when constructed in accordance with UL Design Number U419 so as to achieve a 50 minute fire rating under ASTM E119-09a.
21. The gypsum panel of claim 17 , wherein the gypsum panels are effective to inhibit the transmission of heat through the assembly when constructed in accordance with UL Design Number U423 so as to achieve a 50 minute fire rating under ASTM E119-09a.
22. The gypsum panel of claim 17 , wherein the panel on the first side of the assembly and the panel on the second side of the assembly define an interior cavity of the assembly between the panels, and wherein the interior cavity contains an insulation material selected from mineral wool and fiber glass.
23. The gypsum panel of claim 22 , wherein the gypsum panels are effective to inhibit the transmission of heat through the assembly when constructed in accordance with UL Design Number U419 so as to achieve a one hour fire rating under ASTM E119-09a.
24. The gypsum panel of claim 22 , wherein the gypsum panels are effective to inhibit the transmission of heat through the assembly when constructed in accordance with UL Design Number U423 so as to achieve a one hour fire rating under ASTM E119-09a.
25. The gypsum panel of claim 17 , wherein the mixture further comprises starch.
26. The gypsum panel of claim 25 , wherein the starch is in an amount from about 0.3% to about 3% by weight of stucco.
27. The gypsum panel of claim 25 , wherein the starch is a pregelatinized starch or a functionally equivalent starch, a hydroxyethylated starch, an acid-modified starch or a non-pregelatinized starch.
28. The gypsum panel of claim 17 , wherein the mixture further comprises mineral, carbon, and/or glass fibers.
29. The gypsum panel of claim 28 , wherein the mineral, carbon and/or glass fibers are in an amount from about 0.3% to about 0.9% by weight of stucco.
30. The gypsum panel of claim 17 , the mixture further comprising:
starch in an amount of up to about 3% by weight of stucco; and
mineral, carbon and/or glass fibers.