Dental shaped bodies with continuous shade gradient
What is described is a milling blank having a continuous shade gradient for production of an indirect dental restoration, composed of resin or a resin-based composite. What is also described is a method of producing such a milling blank by mixing two differently coloured pastes with continuous variation of the mixing ratio of the two pastes during the dispensing operation.
1. A milling blank for the production of an indirect dental restoration composed of resin or of a resin-based composite, characterized in that the colour changes continuously from one corner to the diametrically opposite corner and/or from one edge to the opposite edge and/or from one face to the opposite face.
2. The milling blank according to claim 1 , wherein an L* value and/or an a* value and/or a b* value in the L*a*b* colour space change continuously from one corner to the diametrically opposite corner and/or from one edge to the opposite edge and/or from one face to the opposite face.
3. The milling blank according to claim 1 , wherein the L* value in the L*a*b* colour space changes continuously from a value L*1 at a first corner and/or edge and/or face to a value L*2 in each case at the opposite corner and/or edge and/or face, wherein L*2>L*1,
and/or
wherein the a* value in the L*a*b* colour space changes continuously from a value a*1 at a first corner and/or edge and/or face to a value a*2 in each case at the opposite corner and/or edge and/or face, wherein a*2<a*1,
and/or
wherein the b* value in the L*a*b* colour space changes continuously from a value b*1 at a first corner and/or edge and/or face to a value b*2 in each case at the opposite corner and/or edge and/or face, wherein b*2<b*1.
4. The milling blank according to claim 3 , wherein a difference ΔL*=|L*2−L*1| is greater than 2, and/or a difference Δa*=|a*1−a*2| is greater than 0.5, and/or
a difference Δb*=|b*1−b*2| is greater than 1,
wherein the L*a*b* values are measured on 2 mm-thick discs against a white background.
5. The milling blank according to claim 3 , wherein
L*1 is in the range from 50 to 70,
L*2 is in the range from 65 to 85,
a*1 is in the range from 3 to 7,
a*2 is in the range from −2 to 4,
b*1 is in the range from 12 to 22, and
b*2 is in the range from 5 to 15,
wherein the L*a*b* values are measured on 2 mm-thick discs against a white background.
6. The milling blank according to claim 1 , having x, y and z dimensions of at least 5 mm.
7. The milling blank according to claim 1 , the dimensions of which are selected such that it can be used for milling of
a cube having an edge length of 10 mm,
and/or
a cuboid having a square base area having an edge length of 10 mm, and a height of 20 mm.
8. Dental shaped body produced from a milling blank according to claim 1 .
9. Dental moulding according to claim 8 , which is a crown, a partial crown, a bridge, an inlay, an onlay, a veneer, a partly or fully anatomical artificial tooth or an abutment.