View Patent ↗A functionalized silica sorbent is described. The sorbent comprises mesoporous silica nanoparticles having a surface functionalized with a conjugated system comprising an azole and a phenyl. The surface may be functionalized by a Cu-catalyzed click reaction. The nanoparticles have an average particle size of 10-80 nm, and may be used to adsorb phenolic contaminants from aqueous solutions.
1. A functionalized silica sorbent comprising:
porous silica nanoparticles having a surface functionalized with a conjugated system attached by an alkyl chain of length C 8 -C 16 ,
wherein the conjugated system comprises an azole group and a phenyl group, and
wherein the porous silica nanoparticles have an average particle size of 10-80 nm.
2. The functionalized silica sorbent of claim 1 , wherein the porous silica nanoparticles are clustered in agglomerates having an average diameter of 1-4 μm.
3. The functionalized silica sorbent of claim 1 , wherein the porous silica nanoparticles have an average pore size in a range of 4-9 nm.
4. The functionalized silica sorbent of claim 1 , wherein the porous silica nanoparticles have a BET surface area of 200-380 m 2 /g.
5. The functionalized silica sorbent of claim 1 , wherein the porous silica nanoparticles have a total pore volume in a range of 0.380-0.700 cm 3 /g.
6. The functionalized silica sorbent of claim 1 , wherein the conjugated system consists of a triazole group and a phenyl group.
7. The functionalized silica sorbent of claim 6 , wherein the conjugated system is 4-phenyl-1,2,3-triazole.
8. The functionalized silica sorbent of claim 1 , wherein the alkyl chain has a length of C 10 -C 12 .
9. The functionalized silica sorbent of claim 1 , which has 3-12 wt % N relative to a total weight of the functionalized silica sorbent.
10. The functionalized silica sorbent of claim 1 , which has 50-58 wt % Si relative to a total weight of the functionalized silica sorbent.
11. A method for producing the functionalized silica sorbent of claim 1 , comprising:
mixing a silicon alkoxide, an azidoalkyltrialkoxysilane, and a structure directing agent with an acidic solution to produce a reaction mixture;
heating the reaction mixture in an autoclave at 80-120° C. for 18-30 h to produce an azide-functionalized silica; and
mixing the azide-functionalized silica with an aqueous solution, a copper salt, and an arylalkyne for 4-24 h to produce the functionalized silica sorbent.
12. The method of claim 11 , wherein the azidoalkyltrialkoxysilane is azidoundecyltrimethoxysilane.
13. The method of claim 11 , wherein the silicon alkoxide is tetraethyl orthosilicate.
14. The method of claim 11 , wherein the structure directing agent is a nonionic block copolymer.
15. The method of claim 11 , wherein the copper salt is CuSO 4 .
16. A method of adsorbing a contaminant from an aqueous solution, the method comprising:
mixing the functionalized silica sorbent of claim 1 with the aqueous solution comprising the contaminant at a concentration of 1-600 ng/mL,
wherein a concentration of the functionalized silica sorbent after mixing is 1-100 mg/mL, and
wherein at least 85 wt % of the contaminant relative to a total weight of the contaminant is adsorbed by the functionalized silica sorbent in 10-25 min.
17. The method of claim 16 , wherein the contaminant is at least one selected from the group consisting of a dichlorophenol, a trichlorophenol, 2,6-di-tert-butyl-4-methylphenol, 4-tert-octylphenol, and a benzyl-chlorophenol.
18. The method of claim 16 , wherein the functionalized silica sorbent is confined within a porous membrane bag.
19. The method of claim 16 , wherein the aqueous solution further comprises an inorganic salt at a concentration of 0.01-0.2 g/mL.
20. The method of claim 16 , further comprising desorbing the contaminant by sonicating the functionalized silica sorbent with the adsorbed contaminant in an organic solvent for 15-30 min.