Process to produce an engineered carbon
A process for the conversion of hardwood and bamboo to engineered carbon is disclosed. The biomass feedstock of hardwood and bamboo is placed into a holding canister, and the holding canister is lowered into the sealable reactor vessel. The biomass feedstock is ignited, and superheated stream and/or water is metered, or alternately steam is created in situ by introduction of water, into the process. The process is controlled by supplying compressed air and steam, or in situ water, and releasing process gases. The process is performed in an oxygen deprived state. Steam, or in situ water, is injected at the end of the cycle to end the thermal conversion and clean the resulting engineered carbon.
1. A carbon black comprising
a carbon black having
a pore structure of less than 50 nm;
a surface area ranging from 100 to 2000 m 2 /g;
at least 50% of the carbon black having a particle size less than 7.5 μm;
fixed carbon on a dry fixed basis ranging from 97% to 99% by weight;
ash concentration on a dry fixed basis ranging from 0.5% to 3.5% by weight,
moisture content ranging from 2% to 8% by weight, and
20 to 80% of the measured pore widths having pore widths measuring between 2.1 and 2.5 nm,
wherein the carbon black is derived from a renewable biomass feedstock having sizes and shapes within desired ranges comprising hardwood cut into pieces having minor dimensions ranging from 1 to 6 inches, in wedge shapes that are no greater than 6 inches in diameter, or as slab wood originating from logs with diameters ranging up to 12 inches, and in lengths ranging from 4 to 36 inches, and bamboo either in an original cylindrical shape, or cut lengthwise in half, and in lengths ranging from 4 to 36 inches.
2. The carbon black according to claim 1 , having ash concentration on a dry fixed basis of 2% by weight and a moisture content of 5% by weight.
3. The carbon black according to claim 1 , wherein the surface area ranges from 200 to 300 m 2 /g.
4. The carbon black according to claim 1 , comprising 35 to 65% of the measured pore widths having pore widths measuring between 2.1 and 2.5 nm.
5. An engineered carbon comprising
an engineered carbon having
a pore structure of less than 50 nm;
a surface area ranging from 100 to 500 m 2 /g;
fixed carbon on a dry fixed basis ranging from 81% to 95% by weight;
ash concentration on a dry fixed basis ranging from 0.5% to 3.5% by weight;
moisture content ranging from 2% to 8% by weight, and
20 to 80% of the measured pore widths having pore widths measuring between 2.1 and 2.5 nm,
wherein the engineered carbon is produced from a renewable biomass feedstock having sizes and shapes within desired ranges comprising hardwood cut into pieces having minor dimensions ranging from 1 to 6 inches, in wedge shapes that are no greater than 6 inches in diameter, or as slab wood originating from logs with diameters ranging up to 12 inches, and in lengths ranging from 4 to 36 inches, and bamboo either in an original cylindrical shape, or cut lengthwise in half, and in lengths ranging from 4 to 36 inches.
6. The engineered carbon according to claim 5 , having ash concentration on a dry fixed basis of 2% by weight and a moisture content of 5% by weight.
7. The engineered carbon according to claim 5 , wherein the surface area ranges from 200 to 300 m 2 /g.
8. The engineered carbon according to claim 5 , comprising 35 to 65% of the measured pore widths having pore widths measuring between 2.1 and 2.5 nm.
9. The engineered carbon according to claim 5 , wherein at least 50% of the engineered carbon having a particle size less than 7.5 μm.