METHOD OF MANUFACTURING AN ARTICLE BY INJECTION MOULDING, USE OF A COMPATIBILIZER IN A POLYMER RESIN, AND POLYMER RESIN

1 . A method of manufacturing an article, the method comprising injection moulding an article from a polymer resin,

wherein the polymer resin comprises different types of recycled polymer and a compatibilizer comprising inorganic particulate material and a surface treatment agent on a surface of the inorganic particulate material, and

wherein the polymer resin has a MFI @ 2.16 kg/190° C. of equal to or greater than 3.0 g/10 min.

2 - 5 . (canceled)

6 . A method according to claim 1 , wherein

the polymer resin comprises polyethylene in an amount of at least about 10 wt. % and polypropylene in an amount of no more than about 90 wt. %, and

the polyethlene may comprise a mixture of different types of HDPE, LDPE and/or LLDPE.

7 . (canceled)

8 . (canceled)

9 . A method according to claim 1 , wherein the polymer resin is free of virgin polymer.

10 . A method according to claim 1 , wherein the polymer resin further comprises an impact modifier in an amount of less than about 10 wt.

11 . A method according to claim 1 , wherein the compatibilizer is present in an amount of from about 5 wt. % to about 20 wt.

12 . A method according to claim 1 , wherein the inorganic particulate has a d 50 of no greater than about 2.5 μm.

13 . A method according to claim 1 , wherein the surface treatment agent comprises or is a compound having a formula (1):

A-(X—Y—CO) m (O—B—CO) n OH  (1)

wherein

A is a moiety containing a terminating ethylenic bond with one or two adjacent carbonyl groups;

X is O and m is 1 to 4 or X is N and m is 1;

Y is C 1-18 -alkylene or C 2-18 -alkenylene;

B is C 2-6 -alkylene; n is 0 to 5;

provided that when A contains two carbonyl groups adjacent to the ethylenic group, X is N.

14 . A method according to claim 13 , wherein the compound is selected from ß-carboxy ethylacrylate, ß-carboxyhexylmaleimide, 10-carboxydecylmaleimide, 5-carboxy pentyl maleimide and ß-acryloyloxypropanoic acid.

15 . (canceled)

16 . A method according to claim 1 , wherein the inorganic particulate is calcium carbonate.

17 . (canceled)

18 . (canceled)

19 . A polymer resin suitable for use in injection moulding, the polymer resin comprising a mixture of different recycled polymers and from about 5 wt. % to about 20 wt. % compatibilizer comprising inorganic particulate material and a surface treatment agent on a surface of the inorganic particulate material, based on the total weight of the polymer resin,

wherein the polymer resin has a MFI @ 2.16 kg/190° C. of equal to or greater than 3.0 g/10 min, and

wherein the polymer resin comprises at least about 50 wt. % recycled polyethylene, based on the total weight of the polymer composition, and from about 10 wt. % to about 30 wt. % recycled polypropylene, based on the total weight of the polymer resin.

20 . A polymer resin according to claim 19 , further comprising an impact modifier in an amount of less than about 10 wt. %, based on the total weight of the polymer resin.

21 . A polymer resin according to claim 19 , further comprising an antioxidant in an amount of about about 0.1 wt % to about 5 wt. %, based on the total weight of the polymer resin.

22 . A polymer resin according to claim 19 , wherein the inorganic particulate material has d 50 of no greater than about 2.5 μm.

23 . A polymer resin according to claim 19 , wherein the surface treatment agent comprises or is a compound having a formula (1):

A-(X—Y—CO) m (O—B—CO) n OH  (1)

wherein

A is a moiety containing a terminating ethylenic bond with one or two adjacent carbonyl groups;

X is O and m is 1 to 4 or X is N and m is 1;

Y is C 1-18 -alkylene or C 2-18 -alkenylene;

B is C 2-6 -alkylene; n is 0 to 5;

provided that when A contains two carbonyl groups adjacent to the ethylenic group, X is N.

24 . A polymer resin according to claim 23 , wherein the compound is selected from ß-carboxy ethylacrylate, ß-carboxyhexylmaleimide, 10-carboxydecylmaleimide, 5-carboxy pentyl maleimide and ß-acryloyloxypropanoic acid.

25 . A polymer resin according to claim 19 ,

wherein the compatibilizer comprises inorganic particulate material and an organic linker on a surface of the particulate,

wherein the organic linker has an oxygen-containing acid functionality, and wherein the organic linker is a basic form of an organic acid.

26 . A polymer resin according to claim 19 , wherein the inorganic particulate is calcium carbonate.

27 . An article manufactured by injection moulding a polymer resin according to claim 19 .

28 . An article according to claim 27 , wherein the article has one or more of the following:

a) reduced tiger stripes, compared to (i) an article comprising the polymer resin absent the compatibilizer and/or (ii) an article made from the polymer resin composition in which the compatibilizer has been replaced by a polymer-based compatibilizer, or is free of tiger stripes;

b) a flexural modulus which is greater than an article made from the polymer resin in which the compatibilizer has been replaced by a polymer-based compatibilizer, as determined in accordance with ISO 178;

c) a flexural modulus of at least about 900 MPa, as determined in accordance with ISO 178;

d) an impact strength which is greater than an article comprising the polymer resin absent the compatibilizer, as determined in accordance in a Izod notched impact test at 23° C.±2° C. in accordance with ISO 180;

e) an impact strength which is greater than (i) an article comprising the polymer resin absent the compatibilizer, as determined in accordance in a Izod notched impact test at 23° C.±2° C. in accordance with ISO 180 and/or a flexural modulus which is greater than (ii) an article made from the polymer resin in which the compatibilizer has been replaced by a polymer-based compatibilizer, as determined in accordance with ISO 178;

f) an impact strength of at least about 4.0 kJ/m 2 , for example, from about 4.0 kJ/m 2 to about 20 kJ/m 2 , as determined in a Izod notched impact test at 23° C.±2° C. in accordance with ISO 180.

29 . An article according to claim 27 , wherein the article is a portable waste or refuse container, for example, a wheelie bin, or a part or component thereof.