UV blocking film and composition comprising microfibrillated cellulose, a method for producing said film and use of the composition
The present invention relates to an UV blocking film comprising microfibrillated cellulose wherein at least part of the microfibrillated cellulose is microfibrillated cellulose produced from non-chemical modified lignocellulosic material. The invention also relates to a method for producing the film, use of said film as well as a composition having UV blocking properties.
1. An UV blocking film comprising microfibrillated cellulose wherein at least part of the microfibrillated cellulose is microfibrillated cellulose produced from non-chemical modified lignocellulosic material wherein the film comprises 2.5-50% by weight of fiber based material of microfibrillated cellulose produced from non-chemical modified lignocellulosic material; and wherein at least part of the microfibrillated cellulose is microfibrillated cellulose produced from chemical modified lignocellulosic material wherein the film comprises 50-97.5% by weight of fiber based material of microfibrillated cellulose produced from chemical modified lignocellulosic material.
2. The film according to claim 1 wherein the non-chemical modified lignocellulosic material is mechanical pulp.
3. The film according to claim 2 wherein the mechanical pulp is chemithermomechanical pulp (CTMP), thermomechanical pulp (TMP), pressure groundwood (PGW) pulp and/or stone groundwood pulp (SGP).
4. The film according to claim 1 wherein the lignocellulosic material is fiber from coconut shell.
5. The film according to claim 1 wherein the film comprises 5-40% by weight of fiber based material of microfibrillated cellulose produced from non-chemical modified lignocellulosic material.
6. The film according to claim 1 wherein the film also comprises nano-fillers.
7. The film according to claim 1 , wherein the film has a basis weight of less than 50 g/m2.
8. The film according to claim 1 wherein the film has a transmittance of at least 70% for radiation with wavelengths above 400 nm.
9. The film according to claim 1 wherein the film has a transmittance below 70% for radiation with wavelengths below 400 nm.
10. The film according to claim 1 wherein the film comprises 60-95% by weight of fiber based material of microfibrillated cellulose produced from chemical modified lignocellulosic material.
11. The film according to claim 1 , wherein the film has a basis weight of less than 35 g/m2.
12. The film according to claim 1 , wherein the film has a basis weight of less than 25 g/m2.
13. A method for manufacturing a film having UV blocking properties wherein the method comprises the steps of:
providing a first suspension comprising microfibrillated cellulose produced from non-chemical modified lignocellulosic material,
providing a second suspension comprising microfibrillated cellulose produced from chemical modified lignocellulosic material,
mixing the first and second suspension whereby a mixture is obtained,
wherein the mixture comprises the first suspension in an amount of 2.5-50% by weight of the fiber based material and the second suspension in an amount of 50-97.5% by weight of the fiber based material,
conducting the mixture to a wire and thereafter,
dewatering the mixture to form the film.
14. The method as claimed in claim 13 , wherein the microfibrillated cellulose produced from non-chemical modified lignocellulosic material has a Schopper Riegler value)(SR°) of more than 87 SR °.
15. The method according to claim 13 wherein nano-filler is added to the first suspension and/or second suspension.
16. A composition having UV blocking properties wherein said composition comprises microfibrillated cellulose produced from non-chemical modified lignocellulosic material wherein the composition comprises 2.5-50% by weight of fiber based material of microfibrillated cellulose produced from non-chemical modified lignocellulosic material, and wherein said composition comprises microfibrillated cellulose produced from chemical modified lignocellulosic material wherein the film comprises 50-97.5% by weight of fiber based material of microfibrillated cellulose produced from chemical modified lignocellulosic material.
17. The composition according to claim 16 wherein the composition is a paint.
18. The composition according to claim 16 wherein the composition is a sunscreen.
19. The composition according to claim 16 wherein the composition is a coating color.
20. The composition according to claim 16 wherein the composition is a sizing composition.
21. The composition according to claim 16 wherein the composition is a wood impregnation solution.
22. The composition according to claim 16 wherein the composition is a composite comprising a polymer.