Optical filter and optical sensor device

1. An optical filter, comprising:

a base material (i) comprising a resin layer containing a compound (Z) having an absorption maximum in a wavelength region of 700 to 930 nm; and

a dielectric multilayer film formed on at least one surface of the base material (i),

wherein the optical filter satisfies the following requirements (a) to (c):

(a) an average value of transmittances measured in a perpendicular direction to the optical filter in a wavelength region of 380 to 700 nm is not more than 10%;

(b) the optical filter has a light passband (Za) in a wavelength region of not less than 750 nm but not more than 1050 nm, and a maximum transmittance (Td) measured in a perpendicular direction to the optical filter in the light passband (Za) is not less than 45%; and

(c) an absolute value |Xa−Xb| of a difference between a wavelength (Xa) on the shortest wavelength side, at which a transmittance measured in the perpendicular direction to the optical filter is half the transmittance (Td), and a wavelength (Xb) on the shortest wavelength side, at which a transmittance measured at an angle of 30° to the perpendicular direction to the optical filter is half the transmittance (Td), in the light passband (Za), is not more than 15 nm, and the wavelength (Xa) is in the range of 730 to 980 nm, and

wherein the optical filter has a light stopband (Zb) in a region on a longer wavelength side than the light passband (Za), and a minimum transmittance (Te) measured in the perpendicular direction to the optical filter in the light stopband (Zb) is not more than 10%.

2. The optical filter according to claim 1 , wherein the optical filter further satisfies the following requirement (d):

(d) an average value of transmittances measured in the perpendicular direction to the optical filter in the wavelength region of 701 to 750 μm is not more than 15%.

3. The optical filter according to claim 1 , wherein a wavelength (Xc), at which a transmittance measured in the perpendicular direction to the optical filter in the light passband (Za) is maximum, is in the range of 780 to 1000 nm.

4. The optical filter according to claim 3 , wherein a transmittance (Tc) measured at an angle of 30° to the perpendicular direction to the optical filter at the wavelength (Xc) is not less than 45%.

5. The optical filter according to claim 1 , wherein the optical filter further satisfies the following requirement (e):

(e) a maximum transmittance measured in the perpendicular direction to the optical filter in the light passband (Za) is not less than 75%, and an absolute value |Xd−Xe| of a difference between a wavelength (Xd) on the shortest wavelength side, at which a transmittance measured in the perpendicular direction to the optical filter in the light passband (Za) is 70%, and a wavelength (Xe) on the shortest wavelength side, at which a transmittance measured in the perpendicular direction to the optical filter in the wavelength region of not less than 720 nm is 30%, is not more than 30 nm.

6. The optical filter according to claim 1 , wherein the thickness of the optical filter is not more than 180 μm.

7. The optical filter according to claim 1 , wherein the compound (Z) is at least one compound selected from the group consisting of a squarylium-based compound, a phthalocyanine-based compound, a naphthalocyanine-based compound, a croconium-based compound, a hexaphyrin-based compound and a cyanine-based compound.

8. The optical filter according to claim 7 , wherein the squarylium-based compound is a compound represented by the following formula (Z):

wherein in formula (Z), substitution units A and B are each independently any of substitution units represented by the following formulae (I) to (III):

wherein in formulae (I) to (III), a site represented by a wavy line is a binding site to a central 4-membered ring,

each X is independently an oxygen atom, a sulfur atom, a selenium atom, a tellurium atom or —NR 8 —,

R 1 to R 8 are each independently a hydrogen atom, a halogen atom, a sulfo group, a hydroxyl group, a cyano group, a nitro group, a carboxy group, a phosphoric acid group, a —NR g R h group, a —SR i group, a —SO 2 R i group, a —OSO 2 R i group or any one of the following L a to L h , R g and R h are each independently a hydrogen atom, a —C(O)R i group or any one of the following L a to L e , and R i is any one of the following L a to L e ,

(L a ) an aliphatic hydrocarbon group of 1 to 12 carbon atoms

(L b ) a halogen-substituted alkyl group of 1 to 12 carbon atoms

(L e ) an alicyclic hydrocarbon group of 3 to 14 carbon atoms

(L a ) an aromatic hydrocarbon group of 6 to 14 carbon atoms

(L e ) a heterocyclic group of 3 to 14 carbon atoms

(L f ) an alkoxy group of 1 to 12 carbon atoms

(L g ) an acyl group of 1 to 12 carbon atoms, which may have a substituent L

(L h ) an alkoxycarbonyl group of 1 to 12 carbon atoms, which may have a substituent L, and

the substituent L is at least one kind selected from the group consisting of an aliphatic hydrocarbon group of 1 to 12 carbon atoms, a halogen-substituted alkyl group of 1 to 12 carbon atoms, an alicyclic hydrocarbon group of 3 to 14 carbon atoms, an aromatic hydrocarbon group of 6 to 14 carbon atoms and a heterocyclic group of 3 to 14 carbon atoms.

9. The optical filter according to claim 1 , wherein a resin for forming the resin layer is at least one resin selected from the group consisting of a cyclic (poly)olefin-based resin, an aromatic polyether-based resin, a polyimide-based resin, a fluorene polycarbonate-based resin, a fluorene polyester-based resin, a polycarbonate-based resin, a polyamide-based resin, a polyarylate-based resin, a polysulfone-based resin, a polyether sulfone-based resin, a polyparaphenylene-based resin, a polyamideimide-based resin, a polyethylene naphthalate-based resin, a fluorinated aromatic polymer-based resin, a (modified) acrylic-based resin, an epoxy-based resin, an allyl ester-based curing type resin, a silsesquioxane-based ultraviolet curing resin, an acrylic-based ultraviolet curing resin and a vinyl-based ultraviolet curing resin.

10. The optical filter according to claim 1 , wherein the base material (i) comprises a resin substrate (ii) containing the compound (Z).

11. The optical filter according to claim 10 , wherein the resin substrate (ii) further contains a compound (S) having an absorption maximum in the wavelength region of 350 to 699 nm.

12. The optical filter according to claim 10 , wherein the glass transition temperature of the resin substrate (ii) is 130 to 300° C.

13. The optical filter according to claim 10 , wherein a difference between the glass transition temperature of the resin substrate (ii) and the glass transition temperature of the resin contained in the resin substrate (ii) is 0 to 10° C.

14. The optical filter according to claim 1 , wherein the base material (i) further contains a compound (S) having an absorption maximum in the wavelength region of 350 to 699 nm.

15. The optical filter according to claim 1 , wherein the base material (i) contains a compound (S-a) having an absorption maximum in the wavelength region of 350 to 500 nm, a compound (S-b) having an absorption maximum in the wavelength region of 501 to 600 nm and a compound (S-c) having an absorption maximum in the wavelength region of 601 to 699 nm.

16. The optical filter according to claim 15 , wherein a difference in absorption maximum wavelength between the compound (S-a) and the compound (S-b) is 50 to 140 nm, and a difference in absorption maximum wavelength between the compound (S-b) and the compound (S-c) is 30 to 100 nm.

17. The optical filter according to claim 1 , wherein an absolute value |Xg−Xh| of a difference between a wavelength (Xg) on the longest wavelength side, at which a transmittance measured in the perpendicular direction to the optical filter is half the transmittance (Td), and a wavelength (Xh) on the longest wavelength side, at which a transmittance measured at an angle of 30° to the perpendicular direction to the optical filter is half the transmittance (Td), in the light passband (Za), is not more than 30 nm.

18. The optical filter according to claim 1 , wherein the base material (i) further comprises a compound (Y) having an absorption maximum on a longer wavelength side than the light passband (Za).

19. The optical filter according to claim 18 , wherein when a wavelength at which a transmittance measured in the perpendicular direction to the optical filter in the light passband (Za) is maximum is a wavelength (Xc),

an absorption maximum wavelength of the compound (Y) is from the wavelength (Xc)+10 nm to the wavelength (Xc)+100 nm.

20. The optical filter according to claim 1 , which is for an optical sensor device.

21. An optical sensor device equipped with the optical filter according to claim 1 .