Method of producing beta zeolite
Provided is a production method with which it is possible to produce beta zeolite at high purity by suppressing the generation of impurities by a seed crystal addition method that can reduce the environmental burden as much as possible, without using an organic structure-directing agent. This method for producing beta zeolite having a step that mixes and heats an organic-compound-free reaction mixture comprising a silica source, alumina source, alkali source, and water with beta zeolite seed crystals, wherein (I) beta zeolite synthesized without using an organic structure-directing agent and having 90% or more by volume of particles 10 μm or less in diameter in the particle size distribution by a laser diffraction scattering-type particle size distribution measurement method is used, (III) acid-treated zeolite in which the SiO 2 /Al 2 O 3 ratio is 150 or less is prepared by (II) contact treatment with an acidic aqueous solution, and the acid-treated zeolite is used as the beta zeolite seed crystals.
1. A method of producing a beta zeolite comprising: mixing an organic compound-free reaction mixture containing a silica source, an alumina source, an alkaline source and water with a beta zeolite seed crystal and heating the resulting mixture, wherein
(I) a beta zeolite which is synthesized without using an organic structure-directing agent and comprises particles having a particle size of 10 μm or less in an amount of 90% or more on a volume basis in the particle size distribution as determined by a laser diffraction/scattering particle size distribution measuring method,
(II) the beta zeolite is subjected to contact treatment with an aqueous acidic solution, and thereby
(III) an acid-treated zeolite having a SiO 2 /Al 2 O 3 molar ratio of 150 or less is prepared and this is used as the beta zeolite seed crystal.
2. The method of producing a beta zeolite according to claim 1 , wherein (1) and (2) below are used in combination as the beta zeolite seed crystal:
(1) the acid-treated zeolite and
(2) the beta zeolite which is synthesized without using an organic structure-directing agent, comprises particles having a particle size of 10 μm or less in an amount of 90% or more on a volume basis in the particle size distribution and is not subjected to contact treatment with an acidic aqueous solution.
3. The method of producing a beta zeolite according to claim 1 , wherein (1) and (3) below are used in combination as the beta zeolite seed crystal:
(1) the acid treated zeolite and
(3) a calcined crystal of the beta zeolite synthesized using an organic structure-directing agent.
4. The method of producing a beta zeolite according to claim 1 , wherein the reaction mixture has molar ratios described below:
SiO 2 /Al 2 O 3 =8 or more and less than 40,
Na 2 O/SiO 2 =0.05 or more and 0.3 or less and
H 2 O/SiO 2 =5 or more and 50 or less.
5. The method of producing a beta zeolite according to claim 1 , wherein the SiO 2 /Al 2 O 3 molar ratio of the acid-treated zeolite is 100 or less.
6. The method of producing a beta zeolite according to claim 1 , comprising preparing a solid-liquid mixture containing (i) below as the beta zeolite seed crystal and adding the solid-liquid mixture to the reaction mixture, wherein
(i) is a beta zeolite which is synthesized without using an organic structure-directing agent, comprises particles having a particle size of 10 μm or less in an amount of 90% or more on a volume basis in the particle size distribution and is subjected to contact with an acidic aqueous solution.
7. The method of producing a beta zeolite according to claim 6 , comprising using a solid-liquid mixture obtained by mixing (i) above and (ii) below as the beta zeolite seed crystal and adding the solid-liquid mixture to the reaction mixture, wherein
(ii) is a beta zeolite which is synthesized without using an organic structure-directing agent, comprises particles having a particle size of 10 μm or less in an amount of 90% or more on a volume basis in the particle size distribution and is not subjected to contact with an acidic aqueous solution.
8. The method of producing a beta zeolite according to claim 6 , comprising using a solid-liquid mixture obtained by mixing (i) above with (iii) below as the beta zeolite seed crystal and adding the solid-liquid mixture to the reaction mixture, wherein
(iii) is a calcined crystal of beta zeolite synthesized using an organic structure-directing agent.
9. The method of producing a beta zeolite according to claim 1 , wherein particles of the beta zeolite which is synthesized without using an organic structure-directing agent are sorting out by (A) a method of sorting out only crystal particles having a small particle size by adjusting a size of opening of filtration cloth used in filtration, (B) a method of sorting out by using a slurry in which crystals are dispersed and sorting out by sedimentation method, (C) a wet method, or (D) a dry method, prior to being subjected to the contact treatment.