Adhesive dual-component composition based on polyurethane
The invention relates to an adhesive dual-component composition comprising a composition A based on a polyurethane prepolymer with cyclocarbonate terminations and a composition B based on a mixture comprising at least one diamine B1 comprising only two primary amine groups of the —CH 2 —NH 2 type and at least one polyamine B2 comprising at least three primary amine groups of the —CH 2 —NH 2 type. The invention also relates to a multilayer structure produced from the adhesive composition according to the invention and to the method for the production thereof.
1. An adhesive composition comprising:
a composition A comprising at least one cyclocarbonate-terminated polyurethane prepolymer, and
a composition B comprising:
at least one diamine B1 comprising only two —CH 2 —NH 2 groups, and
at least one polyamine B2 comprising at least three —CH 2 —NH 2 groups, wherein the diamine B1:polyamine B2 weight ratio ranges from 30/70 to 70/30.
2. The composition as claimed in claim 1 , wherein the cyclocarbonate-terminated polyurethane prepolymer is obtained by reacting an NCO-terminated polyurethane and a glycerol cyclocarbonate.
3. The adhesive composition as claimed in claim 1 , wherein the cyclocarbonate-terminated polyurethane prepolymer is prepared by a process comprising the following steps:
E1) preparing an NCO-terminated polyurethane prepolymer by a polyaddition reaction comprising reacting at least one polyisocyanate selected from the group consisting of diisocyanates and triisocyanates with at least one polyol selected from the group consisting of polyether polyols and polyester polyols, and mixtures thereof; followed by
E2) reacting the product formed in the first step E1) with at least one glycerol cyclocarbonate in an amount such that all of the NCO groups present in the reaction medium at the end of step E1) react in the presence of the glycerol carbonate.
4. The adhesive composition as claimed in claim 3 , wherein at least one polyol is selected from polyester polyols.
5. The adhesive composition as claimed in claim 1 , wherein the diamine or the mixture of diamines B1 has a primary alkalinity ranging from 3.00 to 20.00 meq/g.
6. The adhesive composition as claimed in claim 1 , wherein the polyamine or the mixture of polyamines B2 has a primary alkalinity from 8.00 to 21.00 meq/g.
7. The adhesive composition as claimed in claim 1 , wherein the composition B has a ratio of the primary alkalinity to the total alkalinity ranging from 0.25 to 0.70.
8. The adhesive composition as claimed in claim 1 , wherein the molar ratio of the number of primary amine functions to the number of cyclocarbonate functions ranges from 0.8 to 1.2.
9. The adhesive composition as claimed in claim 1 , further comprising at least one crosslinking catalyst.
10. A ready-to-use kit comprising the adhesive composition as claimed in claim 1 , wherein the compositions A and B are packaged in two separate compartments.
11. A multilayer structure comprising at least two layers of material bonded together by an adhesive layer, wherein said adhesive layer comprises the adhesive composition as claimed in claim 1 , in a crosslinked state.
12. The multilayer structure as claimed in claim 11 , wherein the adhesive layer has a thickness ranging from 1.5 to 5 μm.
13. The multilayer structure as claimed in claim 11 , comprising at least one layer of aluminum-based material.
14. A process for manufacturing a multilayer structure as claimed in claim 11 , comprising the following steps:
mixing the composition A and the composition B to form a mixture, then
coating said mixture over a surface of a first layer of material to form a coated surface, then
laminating a surface of a second layer of material over said coated surface, then
crosslinking said mixture.
15. The manufacturing process as claimed in claim 14 , wherein the mixture of the composition A and the composition B comprises at least one solvent and wherein the process further comprises a step of evaporating the solvent(s).