Cathode active material for all-solid-state lithium secondary battery
Provided is a novel positive electrode active material capable of suppressing resistance and improving rate characteristics and cycle characteristics while enhancing lithium ionic conductivity, wherein the surface of particles composed of a spinel-type composite oxide containing Li, Mn, O, and two or more other elements is coated with a lithium ion conductive oxide such as LiNbO 3 . Proposed is a positive electrode active material for an all-solid-type lithium secondary battery, wherein the surface of present core particles composed of a spinel-type composite oxide containing Li, Mn, O, and two or more other elements is coated with an amorphous compound containing Li, A (A represents one or more elements selected from the group consisting of Ti, Zr, Ta, Nb, and Al), and O; and the molar ratio (Li/A) of Li relative to the A element in the surface, as obtained by XPS, is 1.0 to 3.5.
1. A positive electrode active material for an all-solid-type lithium secondary battery to be used for an all-solid-type lithium secondary battery,
wherein the surface of particles (referred to as “core particles”) composed of a spinel-type composite oxide containing Li, Mn, O, and two or more other elements is coated with an amorphous compound containing Li, A (A represents one or more elements selected from the group consisting of Ti, Zr, Ta, Nb, and Al), and O; and
the molar ratio (Li/A) of Li relative to the A element in the surface, as obtained by X-ray photoelectron spectroscopy (XPS), is 1.0 to 3.5.
2. The positive electrode active material for an all-solid-type lithium secondary battery according to claim 1 ,
wherein, in the amorphous compound, a halo pattern can be obtained by selected area electron diffraction.
3. The positive electrode active material for an all-solid-type lithium secondary battery according to claim 2 ,
wherein an amount of lithium carbonate present on the surface of the positive electrode active material is less than 2.5 wt % relative to the amount of the positive electrode active material.
4. The positive electrode active material for an all-solid-type lithium secondary battery according to claim 3 ,
wherein the spinel-type composite oxide constituting the core particles is represented by a general formula: Li[Li a Mn 2-a-b-c M1 b M2 c ]O 4-δ (where M1 represents one or more elements selected from the group consisting of Ni, Co, and Fe; M2 represents one or more elements selected from the group consisting of Mg, Ti, Al, Ba, Cr, W, Mo, Y, Zr, and Nb; and the parameters a, b, and c satisfy 0.00≤a≤0.20, 0.20≤b≤1.20, and 0.001≤c≤0.400 respectively).
5. An all-solid-type lithium secondary battery comprising the positive electrode active material for an all-solid-type lithium secondary battery according claim 3 .
6. The positive electrode active material for an all-solid-type lithium secondary battery according to claim 2 ,
wherein the spinel-type composite oxide constituting the core particles is represented by a general formula: Li[Li a Mn 2-a-b-c M1 b M2 c ]O 4-δ (where M1 represents one or more elements selected from the group consisting of Ni, Co, and Fe; M2 represents one or more elements selected from the group consisting of Mg, Ti, Al, Ba, Cr, W, Mo, Y, Zr, and Nb; and the parameters a, b, and c satisfy 0.00≤a≤0.20, 0.20≤b≤1.20, and 0.001≤c≤0.400 respectively).
7. An all-solid-type lithium secondary battery comprising the positive electrode active material for an all-solid-type lithium secondary battery according claim 2 .
8. The positive electrode active material for an all-solid-type lithium secondary battery according to claim 1 ,
wherein an amount of lithium carbonate present on the surface of the positive electrode active material is less than 2.5 wt % relative to the amount of the positive electrode active material.
9. The positive electrode active material for an all-solid-type lithium secondary battery according to claim 8 ,
wherein the spinel-type composite oxide constituting the core particles is represented by a general formula: Li[Li a Mn 2-a-b-c M1 b M2 c ]O 4-δ (where M1 represents one or more elements selected from the group consisting of Ni, Co, and Fe; M2 represents one or more elements selected from the group consisting of Mg, Ti, Al, Ba, Cr, W, Mo, Y, Zr, and Nb; and the parameters a, b, and c satisfy 0.00≤a≤0.20, 0.20≤b≤1.20, and 0.001≤c≤0.400 respectively).
10. An all-solid-type lithium secondary battery comprising the positive electrode active material for an all-solid-type lithium secondary battery according claim 8 .
11. The positive electrode active material for an all-solid-type lithium secondary battery according to claim 1 ,
wherein the spinel-type composite oxide constituting the core particles is represented by a general formula: Li[Li a Mn 2-a-b-c M1 b M2 c ]O 4-δ (where M1 represents one or more elements selected from the group consisting of Ni, Co, and Fe; M2 represents one or more elements selected from the group consisting of Mg, Ti, Al, Ba, Cr, W, Mo, Y, Zr, and Nb; and the parameters a, b, and c satisfy 0.00≤a≤0.20, 0.20≤b≤1.20, and 0.001≤c≤0.400 respectively).
12. An all-solid-type lithium secondary battery comprising the positive electrode active material for an all-solid-type lithium secondary battery according claim 11 .
13. An all-solid-type lithium secondary battery comprising the positive electrode active material for an all-solid-type lithium secondary battery according claim 1 .