Manufacture of tungsten monocarbide (WC) spherical powder
Powder metallurgy, in particular production of tungsten monocarbide spherical powders, which is a major component of metalloceramic hard alloys used for manufacture of tools, drill bits, steel alloying, wear-resistant coating cladding at elements operating in intensive wear conditions. The method includes melting of the starting material, and melt atomization with forming of spherical powder. As starting material a tungsten monocarbide grit is used. Melting and atomization of the material is implemented by continuous filling of grit into a rotating crucible of a centrifugal atomization device under an inert atmosphere and melting it by a plasma arc. After that an annealing of the obtained powder is made at a temperature of 1200-1400° C. during a time necessary for W 2 C breakup with subsequent cooling of the powder in a furnace. And, the production of tungsten monocarbide spherical powder with WC content of more than 70%.
1. A method for the manufacture of tungsten monocarbide (WC) spherical powder said method comprising the steps of:
initial melting of a starting material, and subsequent melt atomization with forming of spherical powder
wherein a grit of tungsten monocarbide is used as the starting material, melting and atomization of the starting material is performed by continuous filling of grit into a rotating crucible of a centrifugal atomization device under an inert atmosphere and melting by plasma arc to form a powder comprising WC, W 2 C, and C, and after that an annealing of the powder is made at a temperature of 1200-1400° C. during a time necessary for W 2 C breakup and subsequent cooling of the powder in a furnace.
2. The method according to claim 1 , wherein the starting material is a grit of tungsten monocarbide WC with a particle size in the interval 20-80 μm.
3. The method according to claim 1 , wherein the annealing of the obtained powder is performed during 1.5-2 hours.
4. The method according to claim 1 , wherein a powder with particle size from 10 μm to 2.5 mm is produced.
5. The method according to claim 1 , wherein the inert atmosphere comprises at least one gas selected from the group consisting of nitrogen, argon, and helium.