COMPOSITIONS COMPRISING CARBON FIBERS AND AT LEAST ONE THERMOPLASTIC POLYOLEFIN ELASTOMER
The present disclosure relates to a composition comprising: (A) from 40 wt % to 95 wt % of a thermoplastic polyolefin elastomer and (B) from 5 wt % to 60 wt % of a carbon fiber component. In certain embodiments, the composition of the present disclosure reaches a high level of stiffness while exhibiting a high level of toughness. Moreover, a decrease in gloss appearance and an improvement in resistance to abrasion are expected.
1 . A composition comprising:
(A) from 40 wt % to 95 wt % of a thermoplastic polyolefin elastomer; and
(B) from 5 wt % to 60 wt % of a carbon fiber component,
wherein the carbon fiber component comprises chopped carbon fibers sized with an epoxy- and phenoxy-based emulsion.
2 . The composition of claim 1 , wherein the thermoplastic polyolefin elastomer is a propylene/alpha-olefin copolymer.
3 . The composition according to any of the preceding claims, wherein the thermoplastic polyolefin elastomer is a propylene-ethylene copolymer.
4 . The composition according to any of the preceding claims, wherein the thermoplastic polyolefin elastomer is a propylene-ethylene copolymer having a density from 0.870 g/cc to 0.900 g/cc as measured by ASTM D792 and a melt flow rate from 0.1 g/10 minutes to 50 g/10 minutes as measured by ASTM D1238 at 230° C./2.16 kg.
5 . The composition according to any of the preceding claims, further comprising a flexural modulus of greater than 3000 MPa.
6 . The composition according to any of the preceding claims, further comprising a Charpy impact strength of greater than 10 kJ/m 2 .