Rubber blend, sulfur-crosslinkable rubber mixture, and vehicle tire
The invention relates to a sulfur-crosslinkable rubber mixture comprising a rubber blend composed of at least one solution-polymerized diene polymer A of high molecular weight and at least one solution-polymerized polymer B of low molecular weight, wherein at least one of polymers A and B has been functionalized at the chain end and/or along the polymer chain and/or at a coupling site with at least one group selected from epoxy groups, hydroxyl groups, carboxyl groups, silane sulfide groups, amino groups, siloxane groups, organosilicon groups, phthalocyanine groups and amino group-containing alkoxysilyl groups, 30 to 300 phr of at least one silica and 1 to 20 phf of at least one substance of formula I) as silane coupling agent (R 1 R 2 R 3 )Si—S 4 —Si(R 3 R 2 R 1 ) II) where R 1 , R 2 , R 3 in the structure may be the same or different and may be selected from linear or branched alkoxy, cycloalkoxy, alkyl, cycloalkyl or aryl groups having 1 to 20 carbon atoms.
1. A rubber blend comprising:
at least one solution-polymerized diene polymer A of high molecular weight, formed from at least one conjugated diene and one or more vinylaromatic compound(s), wherein the one or more vinylaromatic compound(s) have a content of vinylaromatic compound of 0% to 50% by weight, a vinyl content of 8% to 80% by weight based on any diene content present, and wherein the one or more optional vinylaromatic compound(s), has a glass transition temperature Tg according to DSC of −100° C. <Tg<−61° C., a molecular weight Mw according to GPC of more than 350000 g/mol and a polydispersity PD of 1.1<PD<3;
at least one solution-polymerized polymer B of low molecular weight, formed from at least one conjugated diene and one or more vinylaromatic compound(s), or at least one or more vinylaromatic compound(s), wherein the one or more vinylaromatic compound(s) has a content of vinylaromatic compound of 0% to 50% by weight, a vinyl content of 8% to 80% by weight based on any diene content present, and wherein the one or more vinylaromatic compound(s) has a glass transition temperature Tg according to DSC of −32° C. <Tg<+80° C., a molecular weight Mw according to GPC of 1300 g/mol <Mw<10000 g/mol and a polydispersity PD of 1<PD<1.5;
30 to 300 phr of at least one silica; and,
1 to 20 phf of at least one substance of formula I) as a silane coupling agent:
(R 1 R 2 R 3 )Si—S 4 —Si(R 3 R 2 R 1 ) I)
wherein R 1 , R 2 , R 3 in the structure may be the same or different and may be selected from linear or branched alkoxy, cycloalkoxy, alkyl, cycloalkyl or aryl groups having 1 to 20 carbon atoms;
wherein at least one of polymers A and B has been functionalized at the chain end and/or along the polymer chain and/or at a coupling site with at least one group selected from epoxy groups, hydroxyl groups, carboxyl groups, silane sulfide groups, amino groups, siloxane groups, organosilicon groups, phthalocyanine groups and amino group-containing alkoxysilyl groups; and,
and wherein the polymers A and B are combined and processed together to give a rubber blend without solvent to obtain a transportable and processible blend.
2. The rubber blend as claimed in claim 1 , wherein at least the solution-polymerized polymer B of low molecular weight has been functionalized.
3. The rubber blend as claimed in claim 2 , wherein the solution-polymerized diene polymer A of high molecular weight has been functionalized.
4. The rubber blend as claimed in claim 1 , wherein at least one of polymer A and polymer B has been functionalized at the chain end with an amino group-containing alkoxysilyl group and at least one further amino group and/or at least one further alkoxysilyl group and/or at least one further amino group-containing alkoxysilyl group, wherein the amino groups are bonded to the chain end of the polymer chain with or without spacers.
5. The rubber blend as claimed in claim 1 , wherein at least one of the polymers A and B has been functionalized at the chain end and/or along the polymer chain and/or at a coupling site with a silane sulfide group.
6. The rubber blend as claimed in claim 1 , wherein at least one of the polymers A and B has been functionalized at the chain end and/or along the polymer chain and/or at a coupling site with a siloxane group.
7. The rubber blend as claimed in claim 1 , wherein at least one of the polymers A and B has coupling sites.
8. The rubber blend as claimed in claim 1 comprising 5 to 100 phr of the at least one solution-polymerized polymer B of low molecular weight, based on the at least one solution-polymerized diene polymer A of high molecular weight.
9. The rubber blend as claimed in claim 1 having a Mooney viscosity (ML1+4, 100° C. according to ASTM-D 1646) of 40 to 100 Mooney units.
10. The rubber blend as claimed in claim 1 , wherein the proportion of the diene polymer A of the rubber blend in the rubber mixture is at least 50 phr based on the total amount of solid rubbers present in the rubber mixture.
11. The rubber blend as claimed in claim 1 , wherein the at least one substance of formula I) is bis(3-triethoxysilylpropyl) tetrasulfide (TESPT).
12. The rubber blend as claimed in claim 1 , comprising 0.1 to 20 phr of carbon black.
13. A vehicle tire in which at least one component includes the with sulfur-crosslinked rubber mixture as claimed in claim 12 .
14. The vehicle tire as claimed in claim 13 , wherein at least the part of a tread that comes into contact with a driving surface comprises the sulfur-crosslinked rubber mixture.