Rubber blend, sulfur-crosslinkable rubber mixture, and vehicle tire
The invention relates to a sulfur-crosslinkable rubber mixture comprising a rubber blend composed of at least one solution-polymerized diene polymer A of high molecular weight and at least one solution-polymerized polymer B of low molecular weight, wherein at least one of polymers A and B has been functionalized at the chain end and/or along the polymer chain and/or at a coupling site with at least one group selected from epoxy groups, hydroxyl groups, carboxyl groups, silane sulfide groups, amino groups, siloxane groups, organosilicon groups, phthalocyanine groups and amino group-containing alkoxysilyl groups, and as filler at least one silica and/or at least one carbon black in an amount of 25 to 300 phr, wherein the ratio of carbon black to silica in the mixture is 100:0 to 3:97.
1. A rubber blend comprising:
a solution-polymerized diene polymer A of high molecular weight, formed from at least one conjugated diene and one or more optional vinylaromatic compound(s), wherein the one or more optional vinylaromatic compound(s) have a content of vinylaromatic compound of 0% to 50% by weight, a vinyl content of 8% to 80% by weight based on any diene content present, and wherein the one or more optional vinylaromatic compound(s), has a glass transition temperature Tg according to DSC of −100° C.<Tg<+20° C., a molecular weight Mw according to GPC of at least 438020 g/mol and a polydispersity PD of 1.1<PD<3;
a solution-polymerized polymer B of low molecular weight, formed from at least one conjugated diene, at least one conjugated diene and one or more vinylaromatic compound(s), or at least one or more vinylaromatic compound(s), wherein the one or more vinylaromatic compound(s) has a content of vinylaromatic compound of 0% to 50% by weight, a vinyl content of 8% to 80% by weight based on any diene content present, and wherein the one or more vinylaromatic compound(s) has a glass transition temperature Tg according to DSC of −100° C.<Tg<+80° C., a molecular weight Mw according to GPC of 1300 g/mol<Mw<10000 g/mol and a polydispersity PD of 1<PD<1.5; and,
and as filler, at least one optional silica and at least one carbon black in an amount of 25 to 300 phr, wherein the ratio of carbon black to silica in the mixture is 100:0 to 3:97;
wherein at least one of polymers A and B has been functionalized at the chain end and/or along the polymer chain and/or at a coupling site with at least one group selected from epoxy groups, hydroxyl groups, carboxyl groups, silane sulfide groups, amino groups, siloxane groups, organosilicon groups, phthalocyanine groups and amino group-containing alkoxysilyl groups; and, wherein polymers comprised in the rubber blend consist of the solution-polymerized diene polymer A, the solution-polymerized diene polymer B, and a diene rubber selected from the group consisting of synthetic polyisoprene (IR), natural polyisoprene (NR), polybutadiene (BR), and mixtures thereof.
2. The rubber blend as claimed in claim 1 , wherein at least the solution-polymerized polymer B of low molecular weight has been functionalized.
3. The rubber blend as claimed in claim 2 , wherein the solution-polymerized diene polymer A of high molecular weight has been functionalized.
4. The rubber blend as claimed in claim 1 , wherein at least one of polymer A and polymer B has been functionalized at the chain end with an amino group-containing alkoxysilyl group and at least one further amino group and/or at least one further alkoxysilyl group and/or at least one further amino group-containing alkoxysilyl group.
5. The rubber blend as claimed in claim 1 , wherein at least one of the polymers A and B has been functionalized at the chain end and/or along the polymer chain and/or at a coupling site with a silane sulfide group.
6. The rubber blend as claimed in claim 1 , wherein at least one of the polymers A and B has been functionalized at the chain end and/or along the polymer chain and/or at a coupling site with a siloxane group.
7. The rubber blend as claimed in claim 1 , wherein at least one of the polymers A and B has coupling sites.
8. The rubber blend as claimed in claim 1 comprising 5 to 100 phr of the at least one solution-polymerized polymer B of low molecular weight, based on the at least one solution-polymerized diene polymer A of high molecular weight.
9. The rubber blend as claimed in claim 1 having a Mooney viscosity (ML1+4, 100° C. according to ASTM-D 1646) of 40 to 100 Mooney units.
10. The rubber blend as claimed in claim 1 , wherein the proportion of the diene polymer A of the rubber blend in the rubber mixture is at least 50 phr based on the total amount of solid rubbers present in the rubber mixture.
11. A vehicle tire in which at least one component includes the with sulfur-crosslinkable rubber mixture as claimed in claim 1 .
12. The vehicle tire as claimed in claim 11 , wherein at least a part of a tread that comes into contact with a driving surface comprises the sulfur-crosslinked rubber mixture.