Corrosion-resistant non-woven for pipe liner pultrusion applications
A non-woven chopped fiber mat includes a mixture of glass fibers and synthetic fibers. The non-woven mat is formed using a binder composition that includes a binder resin, a coupling agent, and a corrosion inhibitor. The non-woven mat is non-corrosive and resistant to volatile unsaturated monomers such as styrene, but still remains fully compatible with solvent-containing polyester resins, such that it can be used in various pultruded products.
1. A non-woven mat comprising:
a plurality of reinforcing fibers; and
a binder composition comprising a binder resin, a coupling agent, and a corrosion inhibitor,
wherein the binder composition is non-corrosive,
wherein the binder resin comprises a thermoset material, a thermoplastic material, or a combination thereof, and
wherein the non-woven mat exhibits a tensile strength of at least 1.0 lb/ft after being soaked in a 100% styrene monomer for 10 minutes;
wherein the corrosion inhibitor is triethanolamine, wherein said corrosion inhibitor is present in the binder composition from 0.05 to 15.0 wt. %, based on the total solids in the binder composition.
2. The non-woven mat of claim 1 , wherein the plurality of reinforcing fibers comprises at least one of glass fibers, synthetic fibers, and natural fibers.
3. The non-woven mat of claim 1 , wherein the plurality of reinforcing fibers is a mixture of chopped glass fibers and synthetic fibers.
4. The non-woven mat of claim 1 , wherein the binder composition further comprises a defoamer.
5. The non-woven mat of claim 1 , wherein the coupling agent comprises a silane coupling agent.
6. The non-woven mat of claim 1 , wherein the thermoset material comprises at least one of an acrylic material and a urea formaldehyde material.
7. The non-woven mat of claim 1 , wherein the thermoplastic material comprises ethylene vinyl acetate.
8. The non-woven mat of claim 1 , wherein the binder resin comprises from 50.0 to 100 wt. % of the thermoplastic material and from 0 to 50.0 wt. % of the thermoset material, based on the total binder resin.
9. The non-woven mat of claim 1 , wherein the non-woven mat does not exhibit any fiber whitening after curing, as compared to an otherwise identical non-woven mat without the corrosion inhibitor.