Transparent resin composition and transparent resin molded article
To provide a transparent resin composition having excellent optical characteristics, particularly, excellent optical characteristics under high temperature and high humidity. There is provided a transparent resin composition, including: an aromatic polycarbonate resin; and a water-insoluble organic sulfonic acid and/or a metal salt thereof, in which a content of the water-insoluble organic sulfonic acid and/or the metal salt thereof is 0.01 to 3.0 pts·mass to 100 pts·mass of the aromatic polycarbonate resin, and a dissolved amount of the water-insoluble organic sulfonic acid and/or the metal salt thereof is not more than 0.5 g to 100 g of pure water.
1. A transparent resin composition, comprising:
an aromatic polycarbonate resin; and
a water-insoluble organic sulfonic acid and/or a metal salt thereof, wherein the water-insoluble organic sulfonic acid does not comprise a styrene-acrylonitrile copolymer; wherein
a content of the water-insoluble organic sulfonic acid and/or the metal salt thereof is 0.01 to 3.0 pts·mass to 100 pts·mass of the aromatic polycarbonate resin,
solubility of the water-insoluble organic sulfonic acid and/or the metal salt thereof is not more than 0.5 g in 100 g of pure water, and
a total light transmittance of the transparent resin composition is not less than 75% at a wavelength of 380 to 730 nm in the JIS K7136 standard.
2. The transparent resin composition according to claim 1 , wherein
a weight-average molecular weight of the aromatic polycarbonate resin in terms of polystyrene is 36,000 or more and 63,000 or less.
3. The transparent resin composition according to claim 1 , wherein
the aromatic polycarbonate resin includes a recovered polycarbonate resin, and
a content of the recovered polycarbonate resin is from 1 to less than 100 mass % to the total mass of the aromatic polycarbonate resin.
4. The transparent resin composition according to claim 1 , wherein the aromatic polycarbonate resin includes a recovered polycarbonate resin.
5. The transparent resin composition according to claim 1 , wherein
the aromatic polycarbonate resin includes an aromatic polycarbonate compound having 0.01 to 3.0 mol % branch structure.
6. The transparent resin composition according to claim 1 , wherein
the aromatic polycarbonate resin includes an aromatic polycarbonate-polyorganosiloxane copolymer.
7. The transparent resin composition according to claim 1 , further comprising
a light diffusing agent.
8. The transparent resin composition according to claim 7 , wherein
the light diffusing agent is an inorganic particle or an organic particle, and an average particle diameter of the inorganic particle or the organic particle is 0.1 to 50 μm.
9. The transparent resin composition according to claim 7 , wherein
a content of the light diffusing agent is 0.0005 to 6.0 pts·mass to 100 pts·mass of the aromatic polycarbonate resin.
10. The transparent resin composition according to claim 1 , further comprising
a drip preventing agent, wherein
a content of the drip preventing agent is not more than 0.03 pts·mass to 100 pts·mass of the aromatic polycarbonate resin.
11. A transparent resin molded article,
that is obtained by molding the transparent resin composition according to claim 1 .
12. The transparent resin molded article according to claim 11 ,
that is a cover for lighting apparatus.
13. The transparent resin molded article according to claim 11 ,
that is a diffusing cover for lighting apparatus for display.
14. The transparent resin composition according to claim 1 , wherein the water-insoluble organic sulfonic acid is a metal salt of the water-insoluble organic sulfonic acid that includes an aromatic sulfonic acid metal salt compound.
15. The transparent resin composition according to claim 14 , wherein a weight-average molecular weight of the aromatic sulfonic acid metal salt compound in terms of polystyrene is not less than 30,000.
16. The transparent resin composition according to claim 14 , wherein the aromatic sulfonic acid metal salt compound comprises a sulfonic acid metal base, and wherein a content of the sulfonic acid metal base is 0.1 to 10 mol %.
17. The transparent resin composition according to claim 14 , wherein the aromatic sulfonic acid metal salt compound is a potassium salt of polystyrene sulfonic acid.
18. The transparent resin composition according to claim 1 , wherein the total light transmittance of the transparent resin composition is not less than 85% at a wavelength of 380 to 730 nm in the JIS K7136 standard.
19. The transparent resin composition according to claim 1 , wherein a rate of decrease of a total light transmittance of the transparent resin composition after an acceleration test under a condition of 120° C., 100% relative humidity, and 24 hours is within 8% of a total light transmittance of the transparent resin composition before the acceleration test.