Biological tissue rootage face, implant, method for forming biological tissue rootage face, and method for producing implant
A biological tissue rootage face ( 30 ) capable of closely bonding to a biological tissue (H, S) is composed of a biocompatible material and has numerous fingertip-shaped microvilli ( 41 ). The microvilli ( 41 ) have tip diameters in the order of nanometers. An implant ( 1 ) has the biological tissue rootage face ( 30 ) on a surface ( 11, 24 ) configured to root into a biological tissue (H, S). In a method for forming the biological tissue rootage face ( 30 ), a surface of a biocompatible material is subjected to laser nonthermal processing carried out by emitting a laser beam in air, to form numerous fingertip-shaped microvilli ( 41 ). The laser beam is a laser beam of an ultrashort pulse laser.
1. An implant, comprising:
a ceramic sintered compact composed of a biocompatible ceramic material, and
a laser nonthermal processed surface provided on an outer surface of the ceramic sintered compact,
wherein the laser nonthermal processed surface is formed by non-thermally processing the outer surface of the ceramic sintered compact with laser and removing portions of the outer surface that are melted by the laser,
wherein fingertip-shaped microvilli elongate from the laser nonthermal processed surface, the fingertip-shaped microvilli being formed by the nonthermal processing with the laser, and
wherein each of the fingertip-shaped microvilli has a tip diameter of less than 1000 nanometers.
2. The implant according to claim 1 ,
wherein the laser nonthermal processed surface has a groove having a width of 1 μm or more and 50 μm or less and a depth of 1 μm or more and 20 μm or less; and
wherein the fingertip-shaped microvilli are elongated from an inner surface of the groove.
3. The implant according to claim 1 ,
wherein the laser nonthermal processed surface has a groove having a width of 10 μm or more and 500 μm or less and a depth of 5 μm or more and 100 μm or less; and
wherein the fingertip-shaped microvilli are elongated from an inner surface of the groove.
4. The implant according to claim 1 ,
wherein the laser nonthermal processed surface has a large groove having a width of 10 or more and 500 μm or less and a depth of 5 μm or more and 100 μm or less;
wherein the laser nonthermal processed surface has a small groove arranged on an inner surface of the large groove and having a width of 1 μm or more and 50 μm or less and a depth of 1 μm or more and 20 μm or less; and
wherein the fingertip-shaped microvilli are elongated from an inner surface of the small groove.
5. The implant according to claim 1 ,
wherein a three-dimensional surface roughness Sa of the laser nonthermal processed surface is from 500 nm to 800 nm, and
wherein an interface developed area ratio of the laser nonthermal processed surface is from 0.1 to 2.0.
6. A method of forming an implant, comprising:
forming a ceramic sintered compact composed of a biocompatible ceramic material; and
subjecting an outer surface of the ceramic sintered compact to a laser nonthermal process and removing portions of the outer surface melted by a laser light, so as to form a laser nonthermal processed surface on the outer surface and fingertip-shaped microvilli that elongate from the laser nonthermal processed surface,
wherein fingertip-shaped microvilli has a tip diameter of less than 1000 nanometers.
7. The method for forming an implant according to claim 6 ,
wherein the laser nonthermal processed surface has a groove having a width of 1 μm or more and 50 μm or less and a depth of 1 μm or more and 20 μm or less; and
wherein the fingertip-shaped microvilli are elongated from an inner surface of the groove.
8. A method for forming an implant according to claim 6 ,
wherein the laser nonthermal processed surface has a groove having a width of 10 μm or more and 500 μm or less and a depth of 5 μm or more and 100 μm or less; and
wherein the fingertip-shaped microvilli are elongated from an inner surface of the groove.
9. A method for forming an implant according to claim 6 ,
wherein the laser nonthermal processed surface has a large groove having a width of 10 μm or more and 500 μm or less and a depth of 5 μm or more and 100 μm or less;
wherein the laser nonthermal processed surface has a small groove arranged on an inner surface of the large groove and having a width of 1 μm or more and 50 μm or less and a depth of 1 μm or more and 20 μm or less; and
wherein the fingertip-shaped microvilli are elongated from an inner surface of the small groove.