Film-forming material and film
A coating material containing an oxyfluoride of yttrium and having a Fisher diameter of 1.0 to 10 μm and a tap density TD to apparent density AD ratio, TD/AD, of 1.6 to 3.5. The coating material preferably has a pore volume of pores with a diameter of 100 μm or smaller of 1.0 cm 3 /g or less as measured by mercury intrusion porosimetry. A coating containing an oxyfluoride of yttrium and having a Vickers hardness of 200 HV0.01 or higher. The coating preferably has a fracture toughness of 1.0×10 2 Pa·m 1/2 or higher.
1. A coating material comprising an oxyfluoride of yttrium and having a Fisher diameter of 1.0 to 10 μm and a ratio TD/AD of a tap density TD to an apparent density AD, of 1.6 to 3.5 wherein the tap density TD and the apparent density AD are measured in accordance with Japanese Industrial Standards, JIS Z 2512 and JIS K 5101, respectively.
2. The coating material according to claim 1 ,
wherein the coating material has a pore volume of pores with a diameter of 100 μm or smaller of 1.0 cm 3 /g or less as measured by mercury intrusion porosimetry.
3. The coating material according to claim 2 ,
wherein the coating material has an angle of repose of 40° or greater.
4. The coating material according to claim 3 ,
wherein the tap density TD is in a range of 1.0 g/cm 3 to 2.0 g/cm 3 .
5. The coating material according to claim 3 ,
wherein the tap density TD is in a range of 1.2 g/cm 3 to 1.8 g/cm 3 .
6. The coating material according to claim 2 ,
wherein the coating material has the ratio TD/AD of 1.7 to 3.2.
7. The coating material according to claim 2 ,
wherein the coating material has the ratio TD/AD of 1.8 to 3.0.
8. The coating material according to claim 2 ,
wherein the tap density TD is in a range of 1.0 g/cm 3 to 2.0 g/cm 3 .
9. The coating material according to claim 2 ,
wherein the tap density TD is in a range of 1.2 g/cm 3 to 1.8 g/cm 3 .
10. The coating material according to claim 1 ,
wherein the coating material has an angle of repose of 40° or greater.
11. The coating material according to claim 10 ,
wherein the coating material has the ratio TD/AD of 1.7 to 3.2.
12. The coating material according to claim 10 ,
wherein the coating material has the ratio TD/AD of 1.8 to 3.0.
13. The coating material according to claim 10 ,
wherein the tap density TD is in a range of 1.0 g/cm 3 to 2.0 g/cm 3 .
14. The coating material according to claim 10 ,
wherein the tap density TD is in a range of 1.2 g/cm 3 to 1.8 g/cm 3 .
15. The coating material according to claim 1 ,
wherein the coating material has the ratio TD/AD of 1.7 to 3.2.
16. The coating material according to claim 1 ,
wherein the coating material has the ratio TD/AD of 1.8 to 3.0.
17. The coating material according to claim 1 ,
wherein the tap density TD is in a range of 1.0 g/cm 3 to 2.0 g/cm 3 .
18. The coating material according to claim 1 ,
wherein the tap density TD is in a range of 1.2 g/cm 3 to 1.8 g/cm 3 .
19. A powder for a coating material, the powder comprising an oxyfluoride of yttrium and having a Fisher diameter of 1.0 to 10 μm and a ratio TD/AD of a tap density TD to an apparent density AD, of 1.6 to 3.5 wherein the tap density TD and the apparent density AD are measured in accordance with Japanese Industrial Standards, JIS Z 2512 and JIS K 5101, respectively.