Disclosed is a method for the use, as fire-retardant, of an aqueous composition including chitosan and at least one mineral filler, the inorganic filler being for example chosen from the group of mineral fillers in laminae, in particular chosen from the group consisting of talc, montmorillonite, saponite, sepiolite, bentonite, smectite, hectorite, kaolinite, halloysite and mica, and mixtures thereof.
1. A fire-retardant treatment method of a surface comprising the application on said surface of an aqueous composition consisting of water, chitosan, at least one mineral filler, said mineral filler being talc, and at least one acid selected from the group consisting of: acetic acid, hydrochloric acid, formic acid, L-ascorbic acid, L-glutamic acid, lactic acid, maleic acid, malic acid, and succinic acid, and mixtures thereof, and optionally at least one surfactant and/or at least one phosphorus additive.
2. The method according to claim 1 , wherein the acid is acetic acid.
3. The method according to claim 1 , wherein the content by weight of chitosan is between 20% and 99.99% by weight relative to the weight of dry extract of the mixture formed by chitosan and the mineral filler, and the content by weight of mineral filler is between 0.01% and 80% by weight relative to the weight of dry extract of the mixture formed by chitosan and the mineral filler.
4. The method according to claim 1 , wherein the aqueous composition comprises from 0.01% to 25% by weight of dry extract of the mixture formed by chitosan and the mineral filler with respect to the total weight of the composition.
5. The method according to claim 1 , wherein the aqueous composition has an acidic pH.
6. The method according to claim 1 , wherein the number-average molar mass of chitosan is between 50,000 g/mol and 200,000 g/mol.
7. The method according to claim 1 , wherein the degree of deacetylation of chitosan is between 75% and 95%.
8. The method according to claim 1 , wherein the aqueous composition has a dynamic viscosity measured at 25° C. and a shear rate of 2 s −1 between 0.1 Pa·s and 1000 Pa·s.
9. The method according to claim 1 , wherein the aqueous composition comprises from 75% to 99.99% by weight of water relative to the total weight of the composition.
10. The method of fire-retarding a surface of claim 1 , the surface comprising wood, natural fibers or synthetic fibers.
11. The method of claim 10 , wherein the aqueous composition is applied by dipping or spraying.
12. The method according to claim 2 , wherein the content by weight of chitosan is between 20% and 99.99% by weight relative to the weight of dry extract of the mixture formed by chitosan and the mineral filler, and the content by weight of mineral filler is between 0.01% and 80% by weight relative to the weight of dry extract of the mixture formed by chitosan and the mineral filler.
13. The method according to claim 1 , wherein the content by weight of chitosan is between 20% and 99.99% by weight relative to the weight of dry extract of the mixture formed by chitosan and the mineral filler, and the content by weight of mineral filler is between 0.01% and 80% by weight relative to the weight of dry extract of the mixture formed by chitosan and the mineral filler.
14. The method according to claim 2 , wherein the aqueous composition comprises from 0.01% to 25% by weight of dry extract of the mixture formed by chitosan and the mineral filler with respect to the total weight of the composition.
15. The method according to claim 1 , wherein the aqueous composition comprises from 0.01% to 25% by weight of dry extract of the mixture formed by chitosan and the mineral filler with respect to the total weight of the composition.
16. The method according to claim 3 , wherein the aqueous composition comprises from 0.01% to 25% by weight of dry extract of the mixture formed by chitosan and the mineral filler with respect to the total weight of the composition.
17. The method according to claim 1 , wherein the aqueous composition has a pH between 3 and 6.
18. A method for the fire-retardant treatment in the mass of a material comprising wood, natural fibers or synthetic fibers, wherein the method comprises the addition during the manufacture of the material of an aqueous composition as defined in claim 1 to the constituent elements of the material before it is formed.
19. The method of mass fire-retardant treatment of a material according to claim 18 , wherein the formation is a formation into a panel.