Glaze for a ceramic article
The glaze is prepared from the following raw materials in percentage by weight: Fire Clay 10%-25%, Feldspar 30%-40%, Sand 30%-40%, Calcium Silicate 8%-12%, Graphane (i.e., disordered crystalline and hydrogenated double bounded Carbon) 5%-15% or C-doped Boron Nitride (CBN) 5%-15%, various metal oxides as pigments and water. This glaze is applied on the standard glazing operation in the ceramic insulator manufacturing process and is fired in a controlled inert-gas atmosphere.
1. A glaze composition for a ceramic article, comprising:
5 wt %-15 wt % Graphane in the glaze composition.
2. The glaze composition for a ceramic article according to claim 1 , further comprising:
5 wt %-25 wt % Fire Clay in the glaze composition;
30 wt %-40 wt % Feldspar in the glaze composition;
17 wt %-40 wt % Sand in the glaze composition; and
8 wt %-23 wt % Silicate in the glaze composition.
3. The glaze composition for a ceramic article according to claim 1 , further comprising:
10 wt %-25 wt % Fire Clay in the glaze composition;
30 wt %-40 wt % Feldspar in the glaze composition;
30 wt %-40 wt % Sand in the glaze composition; and
8 wt %-12 wt % Calcium Silicate in the glaze composition.
4. The glaze composition for a ceramic article according to claim 1 , further comprising:
5 wt %-7.5 wt % Fire Clay in the glaze composition;
30 wt %-38 wt % Feldspar 75K20 & 55NaK60 in the glaze composition;
17 wt %-22 wt % Quartz sand in the glaze composition;
5 wt %-7.5 wt % Wollastonite in the glaze composition;
5 wt %-4.7 wt % Soapstone calcined DIN100 in the glaze composition;
7 wt %-10.5 wt % ZrSiO4 in the glaze composition;
0.8 wt %-3.8 wt % Calcite Carolith in the glaze composition; and
5 wt %-7.5 wt % Chamotte in the glaze composition.
5. The glaze composition according to claim 1 , further comprising:
at least one of a metal oxide and a pigment.
6. A ceramic article comprising:
a surface glaze made of a glaze composition, wherein the glaze composition comprises 5 wt %-15 wt % Graphane.
7. The ceramic article according to claim 6 , wherein the ceramic article comprises a ceramic isolator.
8. The ceramic article according to claim 7 , wherein the ceramic insulator is a high-voltage ceramic isolator.
9. The ceramic article according to claim 8 , wherein the high-voltage ceramic isolator accommodates voltages greater than 1,000 volts.
10. The ceramic article according to claim 6 , wherein the ceramic article comprises porcelain.
11. The ceramic article according to claim 6 , wherein the surface glaze comprises a water-repelling surface.
12. The ceramic article according to claim 6 , wherein the surface glaze comprises hydrophobic surface.
13. The ceramic article according to claim 6 , wherein the glaze composition further comprises
5 wt %-25 wt % Fire Clay in the glaze composition;
30 wt %-40 wt % Feldspar in the glaze composition;
17 wt %-40 wt % Sand in the glaze composition; and
8 wt %-23 wt % Silicate in the glaze composition.
14. The ceramic article according to claim 6 , wherein the glaze composition further comprises
10 wt %-25 wt % Fire Clay in the glaze composition;
30 wt %-40 wt % Feldspar in the glaze composition;
30 wt %-40 wt % Sand in the glaze composition; and
8 wt %-12 wt % Calcium Silicate in the glaze composition.
15. The ceramic article according to claim 6 , wherein the glaze composition further comprises
5 wt %-7.5 wt % Fire Clay in the glaze composition;
30 wt %-38 wt % Feldspar 75K20 & 55NaK60 in the glaze composition;
17 wt %-22 wt % Quartz sand in the glaze composition;
5 wt %-7.5 wt % Wollastonite in the glaze composition;
5 wt %-4.7 wt % Soapstone calcined DIN100 in the glaze composition;
7 wt %-10.5 wt % ZrSiO4 in the glaze composition;
0.8 wt %-3.8 wt % Calcite Carolith in the glaze composition; and
5 wt %-7.5 wt % Chamotte in the glaze composition.
16. The ceramic article according to claim 6 , wherein the glaze composition further comprises at least one of a metal oxide and a pigment.
17. The ceramic article according to claim 16 , wherein the metal oxide is at least one of Fe 2 O 3 , Cr 2 O 3 , MnO, NiO, CoO, ZrO 2 and TiO 2 .
18. The glaze composition according to claim 5 , wherein the metal oxide is at least one of Fe 2 O 3 , Cr 2 O 3 , MnO, NiO, CoO, ZrO 2 and TiO 2 .
19. The glaze composition according to claim 1 , further comprising water.