Use of a coating on a chromium-free tinplate substrate
Use of a coating composition on a chromium free tinplate substrate, the coating composition comprising: a polyester material, and benzoguanamine or a derivative thereof, wherein the coating composition is substantially free of bisphenol A (BPA), bisphenol F (BPF), bisphenol A diglycidyl ether (BADGE) and bisphenol F diglycidyl ether (BFDGE).
1. A coating system on a chromium free tinplate substrate the coating system comprising:
an undercoat coating composition comprising a polyester material, and a crosslinking material comprising benzoguanamine or a derivative thereof, wherein the crosslinking material further comprises a phenolic resin and an isocyanate resin; and
an overcoat coating composition comprising a powder composition comprising a further polyester material,
wherein the undercoat coating composition is substantially free of bisphenol A (BPA), bis phenol F (BPF), bisphenol A diglycidyl ether (BADGE) and bisphenol F diglycidyl ether (BFDGE).
2. The coating system of claim 1 , wherein the undercoat coating composition comprises at least 4.5 wt. % of the benzoguanamine or a derivative thereof based on the total solid weight of the undercoat coating composition.
3. The coating system of claim 1 , wherein the powder coating composition is a thermoplastic coating composition.
4. A food or beverage can at least partially formed from a chromium free tinplate material, wherein the chromium free tinplate material is coated on at least a portion thereof with the coating system of claim 1 .
5. The food or beverage can of claim 4 , wherein the coating system is applied to a seam line or weld along the body of the food or beverage can.
6. The coating system of claim 1 , when cured, has a flexibility of at least 20 mm as measured according to the draw and re-draw test method with processing in 1% salt (NaCl) solution in tap water at 130° C. for 60 minutes and a scratch resistance of at least 700 g as measured according to ISO Standard 1518-1:2011.