Sheetlike composite for producing dimensionally stable food and drink product containers having a polymer layer having a ratio of aromatic groups to carbonyl groups

1. A sheetlike composite comprising, as layers of a layer sequence in the direction from an outer face of the sheetlike composite to an inner face of the sheetlike composite,

a) first colour application, which is a chromatic ink application,

b) a first polymer layer, which is a white primer layer,

c) a further polymer layer, which is a polyolefin layer,

d) a carrier layer, and

e) a barrier layer,

wherein the first polymer layer is characterized by a ratio of a proportion of aromatic groups in the first polymer layer to a proportion of carbonyl groups in the first polymer layer in a range from 0.18 to 0.34,

wherein the ratio of the proportion of aromatic groups in the first polymer layer to the proportion of carbonyl groups in the first polymer layer is determined by

measuring an ATR spectrum that covers a wave number range from 3500 to 1400 cm −1 with a resolution of 4 cm −1 is recorded at 45° by means of a diamond as detector tip, and

calculating the ratio of the area of a maximum of the ATR spectrum in the wave number range from 1590 to 1610 cm −1 to the area of a maximum of the ATR spectrum in the wave number range from 1720 to 1740 cm −1 ,

wherein the first polymer layer is further characterized by a ratio of a proportion of aliphatic groups in the first polymer layer to the proportion of carbonyl groups in the first polymer layer in a range from 0.40 to 0.60,

wherein the ratio of the proportion of aliphatic groups in the first polymer layer to the proportion of carbonyl groups in the first polymer layer is determined by

measuring an ATR spectrum that covers a wave number range from 3500 to 1400 cm −1 with a resolution of 4 cm −1 is recorded at 45° by means of a diamond as detector tip, and

calculating the ratio of the area of a maximum of the ATR spectrum in the wave number range from 2900 to 2950 cm −1 to the area of a maximum of the ATR spectrum in the wave number range from 1720 to 1740 cm −1 .

2. The sheetlike composite according to claim 1 , wherein the first polymer layer further comprises a first colorant in a proportion in a range from 10 to 50% by weight, based on the weight of the first polymer layer.

3. A container precursor comprising the sheetlike composite according to claim 1 .

4. A closed container comprising the sheetlike composite according to claim 1 .

5. A process for producing the sheetlike composite according to claim 1 , the process comprising, as process steps,

a) providing a sheetlike composite precursor comprising, as mutually superposing layers of a layer sequence,

i) the further polymer layer,

ii) the carrier layer, and

iii) the barrier layer;

b) overlaying the carrier layer with a liquid first polymer layer precursor composition on a side facing away from the barrier layer and obtaining the first polymer layer from the liquid first polymer layer precursor composition,

c) overlaying the carrier layer with a liquid first colour application precursor composition on a side facing away from the barrier layer and obtaining the first colour application from the liquid first colour application precursor composition, wherein the liquid first polymer layer precursor composition is characterized by a ratio

of a proportion of aromatic groups in the liquid first polymer layer precursor composition to a proportion of aliphatic groups in the liquid first polymer layer precursor composition in a range from 0.30 to 0.80,

wherein the ratio of the proportion of aromatic groups in the liquid first polymer layer precursor composition to the proportion of aliphatic groups in the liquid first polymer layer precursor composition is determined by

measuring an ATR spectrum that covers a wave number range from 3500 to 1400 cm −1 with a resolution of 4 cm −1 is recorded at 45° by means of a diamond as detector tip, and

calculating the ratio of the area of a maximum of the ATR spectrum in the wave number range from 1590 to 1610 cm −1 to the area of a maximum of the ATR spectrum in the wave number range from 2900 to 2950 cm −1 .

6. A sheetlike composite obtainable by the process according to claim 5 .

7. A process comprising, as process steps,

a. providing the sheetlike composite according to claim 1 , wherein the sheetlike composite further comprises a first longitudinal rim and a further longitudinal rim;

b. folding the sheetlike composite; and

c. contacting and joining the first longitudinal rim to the further longitudinal rim, thereby obtaining a longitudinal seam.

8. A container precursor obtainable by the process according to claim 7 .

9. A process comprising, as process steps,

A) providing the container precursor according to claim 3 ;

B) forming a base region of the container precursor by folding the sheetlike composite;

C) closing the base region;

D) filling the container precursor with a food or drink product, and

E) closing the container precursor in a top region, thereby obtaining a closed container.

10. A closed container obtainable by the process according to claim 9 .