Composition and method for generating a shade gradient in zirconia dental restoration
Disclosed are compositions and methods for bleaching and optionally coloring a shaded zirconia, particularly mono-chromatic pre-shaded dental zirconia. The compositions and methods are useful in generating a shade gradient in milled dental restorations. The compositions comprise metal salts or complex dissolved in a solvent.
1. A method of generating a color gradient by bleaching a pre-shaded zirconia, the method comprising:
applying, to the pre-shaded zirconia, a liquid comprising a metal compound or metal compounds comprising one or more metal selected from zinc, gallium, and aluminum in an amount sufficient to cause bleaching by the formation of oxides in the pre-shaded zirconia after sintering at a temperature greater than or equal to 1450° C., and optionally solvent,
wherein the liquid reduces the intensity of color in the pre-shaded zirconia, and
wherein the liquid substantially maintains the flexural strength of the pre-shaded zirconia.
2. The method of claim 1 , wherein the metal compound is a metal salt or complex comprising a metal and a counterpart selected from halides (Cl, F, Br, and I), nitrate, acetate, sulfate, lactate, propionate, formate, and alkoxides.
3. The method of claim 1 , wherein the metal compound is a solid salt or complex of zinc, aluminum, or gallium and is present at about 0.1 wt % to about 80 wt % by weight of the bleaching liquid.
4. The method of claim 1 , wherein the metal compound is a liquid metal compound of zinc, aluminum, or gallium and is present at about 0.1 wt % to about 100 wt % of the bleaching liquid.
5. The method of claim 1 , wherein the metal is selected from zinc, gallium, and aluminum.
6. The method of claim 2 , wherein the metal salt or complex is selected from:
Conc.
salt/complex
(wt %)
ZnCl 2
1-80
Zn(NO 3 ) 2 •6H 2 O
1-80
Ga(NO 3 ) 3 • x H 2 O
1-80
Al(NO 3 ) 3 •9H 2 O
1-80