Polyolefin gel processing composition containing an inorganic acid scavenger and method using same
A polymer composition for producing gel extruded articles is described. The polymer composition contains polyethylene particles combined with a plasticizer and an acid scavenger. In accordance with the present disclosure, the acid scavenger is an inorganic compound that is insoluble in the plasticizer and/or any extractions solvents used during the process. In one embodiment, the acid scavenger is a magnesium aluminum hydroxide carbonate.
1. A polymer composition for producing gel extruded articles comprising:
a plasticizer;
high density polyethylene particles combined with the plasticizer, and
an acid scavenger, the acid scavenger comprising an inorganic compound that is insoluble in the plasticizer, the inorganic compound comprising an oxide, a carbonate, a silicate, or mixtures thereof, and wherein the acid scavenger is present in the polymer composition in an amount less than about 150 ppm on a weight basis.
2. A polymer composition as defined in claim 1 , wherein the acid scavenger comprises a carbonate.
3. A polymer composition as defined in claim 1 , wherein the acid scavenger comprises a hydrotalcite.
4. A polymer composition as defined in claim 1 , wherein the acid scavenger is present in the composition in an amount less than about 100 ppm on a weight basis.
5. A polymer composition as defined in claim 1 , wherein the high density polyethylene particles are present in the composition in an amount up to about 50% by weight.
6. A polymer composition as defined in claim 1 , wherein the plasticizer comprises mineral oil, a paraffinic oil, a hydrocarbon, an alcohol, an ether, an ester, or mixtures thereof.
7. A polymer composition as defined in claim 1 , wherein the high density polyethylene has a molecular weight of greater than about 2,000,000 g/mol.
8. A polymer composition as defined in claim 1 , wherein the high density polyethylene is a Ziegler-Natty catalyzed ultrahigh molecular weight polyethylene.
9. A polymer composition as defined in claim 1 , wherein the plasticizer comprises decaline, xylene, dioctyl phthalate, dibutyl phthalate, stearyl alcohol, oleyl alcohol, decyl alcohol, nonyl alcohol, diphenyl ether, n-decane, n-dodecane, octane, nonane, kerosene, toluene, naphthalene, tetraline, monochlorobenzene, camphene, methane, dipentene, methylcyclopentandiene, tricyclodecane, 1,2,4,5-tetramethyl-1,4-cyclohexadiene, or mixtures thereof.
10. A process for producing polymer articles comprising:
forming the polymer composition as defined in claim 1 into a gel-like composition;
extruding the gel-like composition through a die to form a polymer article, the polymer article comprising fibers, a film, or a membrane.
11. A process as defined in claim 10 , further comprising the step of removing at least part of the plasticizer from the polymer article.
12. A process as defined in claim 10 , wherein the resulting polymer article contains the acid scavenger in an amount greater than about 10 ppm.
13. A process as defined in claim 10 , wherein an extraction solvent is added to the polymer composition during the process in order to facilitate removal of the plasticizer from the polymer article, the acid scavenger being insoluble in the extraction solvent.
14. A process as defined in claim 13 , wherein the extraction solvent comprises dichloromethane.
15. A polymer composition for producing gel extruded articles comprising:
a plasticizer;
high density polyethylene particles combined with the plasticizer, and
an acid scavenger, the acid scavenger comprising an inorganic compound that is insoluble in the plasticizer, the inorganic compound comprising an oxide, a carbonate, a silicate, or mixtures thereof, and
wherein the plasticizer is present in the polymer composition in an amount greater than about 90% by weight.