IP Library Granted Patent US 12,545,766
Granted Patent B2
US 12,545,766 · App. 16/375,525 · Granted Feb 10, 2026

Curable polymer resins for 3D-printable hierarchical nanoporous foams and aerogels

Inventors: Siwei Liang (Dublin, CA); Theodore F. Baumann (Discovery Bay, CA); Juergen Biener (San Leandro, CA); Monika M. Biener (San Leandro, CA); Bryan D. Moran (Pleasanton, CA); James Oakdale (Castro Valley, CA); Jianchao Ye (Tracy, CA)
Assignee: Lawrence Livermore National Security, LLC
C08J3/075B29C64/112B29C64/153C08F2/48C08J9/286C08K3/042C08L57/00B33Y10/00B33Y70/10B33Y80/00C08J2205/026C08J2205/044C08J2323/00C08J2333/08C08J2333/10C08J2341/00C08J2363/00C08J2375/00C08L2203/14
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 12,545,766
App. No.
16/375,525
Granted
Feb 10, 2026
Kind
B2
Abstract

In one embodiment, a mixture includes a polyfunctional monomer having at least one functional group amenable to polymerization, a porogen, and a polymerization initiator. In another embodiment, a product includes a porous three-dimensional structure formed by additive manufacturing, where the porous three-dimensional structure has ligaments arranged in a geometric pattern, the ligaments defining pores therebetween. The pores have an average diameter greater than about 10 microns, where an average length scale of the ligaments is greater than 100 nanometers. The ligaments are nanoporous, where at least 80% of a volume measured according to outer dimensions of the porous three-dimensional structure corresponds to the pores.

Claims (37)

1 . A mixture comprising:

a monomer having at least one functional group amenable to polymerization;

a porogen;

a polymerization initiator; and

a polymerization inhibitor present at an effective amount to prevent polymerization of an unirradiated portion of the mixture after laser irradiation of a portion of the mixture,

wherein the mixture is configured to undergo phase segregation upon the laser irradiation whereby the monomer transforms from a liquid to a self-supporting polymeric solid and the porogen remains a liquid within nanopores of the self-supporting polymeric solid,

wherein the porogen is present in an effective amount to cause the self-supporting polymeric solid to have a nanoporosity,

wherein the polymerization inhibitor is present in the mixture in a concentration greater than 50,000 ppm.

2 . The mixture as recited in claim 1 , wherein the at least one functional group amenable to polymerization is selected from the group consisting of: acrylate, methacrylate, epoxide, olefin, isocyanate, and mercapto+olefin.

3 . The mixture as recited in claim 1 , wherein the monomer is present in a polymer having a plurality of monomers in a chain thereof.

4 . The mixture as recited in claim 1 , wherein the porogen is a non-reactive component.

5 . The mixture as recited in claim 1 , wherein the porogen is a liquid solvent.

6 . The mixture as recited in claim 1 , wherein the porogen is miscible with the monomer.

7 . The mixture as recited in claim 1 , wherein a concentration of the monomer in the mixture is in a range of about 2 wt % to less than 100 wt % of weight of total mixture.

8 . The mixture as recited in claim 1 , wherein a concentration of the porogen in the mixture is in a range of greater than 0 wt % to about 98 wt % of weight of total mixture.

9 . The mixture as recited in claim 1 , wherein a ratio of the monomer to the porogen is in a range of about 2 parts to 98 parts (2:98) to about 50 parts to 50 parts (50:50) on the basis of weight.

10 . The mixture as recited in claim 1 , wherein the polymerization initiator is a photoinitiator.

11 . The mixture as recited in claim 1 , wherein a concentration of the polymerization initiator in the mixture is in a range of about 0.05 wt % to about 1.0 wt % of weight of total mixture.

12 . The mixture as recited in claim 1 , comprising a photoabsorber.

13 . An ink comprising:

a polyfunctional monomer having a single monomeric unit and at least two functional groups amenable to polymerization;

a porogen;

a polymerization initiator; and

a polymerization inhibitor,

wherein the polymerization inhibitor is present in an effective amount to allow formation of a self-supporting structure having a total porosity in a range greater than 80% by volume,

wherein the porogen is present in an effective amount to cause the self-supporting structure to have a nanoporosity,

wherein the amount of the polymerization inhibitor is in a range of about 2.2 wt. % to about 5.0 wt. % of the total mixture.

14 . The ink as recited in claim 13 , wherein at least one of the at least two functional groups amenable to polymerization is selected from the group consisting of: acrylate, methacrylate, epoxide, olefin, isocyanate, and mercapto+olefin.

15 . The ink as recited in claim 13 , wherein the ink is physically characterized as being extrudable into self-supporting ligaments arranged in a geometric pattern having pores defined between the ligaments.

16 . The ink as recited in claim 13 , wherein a concentration of the polyfunctional monomer in the ink is in a range of about 2 wt % to less than 100 wt % of weight of total ink.

17 . The ink as recited in claim 13 , wherein a ratio of the polyfunctional monomer to the porogen is in a range of about 2 parts to 98 parts (2:98) to about 50 parts to 50 parts (50:50).

18 . The mixture as recited in claim 1 , wherein the mixture is optically transparent.

19 . The mixture as recited in claim 1 , wherein the porogen is configured to not participate in the transformation of the monomer into a solid.

20 . The mixture as recited in claim 1 , wherein the mixture is a resin mixture configured to be printed into a self-supporting three-dimensional structure using light-directed printing.

21 . The mixture as recited in claim 1 , wherein the mixture is configured to form a structure having a porosity in a range of greater than 91% to about 98%.

22 . The mixture as recited in claim 1 , wherein a ratio of the monomer to the porogen is in a range of greater than 1:25 to 1:49 on the basis of weight.

23 . The mixture as recited in claim 13 , wherein the amount of the polymerization inhibitor is in a range of greater than 0.5 wt. % to about 5.0 wt. % of the total mixture.

Assignments (2)
CONFIRMATORY LICENSE (SEE DOCUMENT FOR DETAILS) Recorded Oct 16, 2020
From: LAWRENCE LIVERMORE NATIONAL SECURITY, LLC
To: U.S. DEPARTMENT OF ENERGY
Reel/Frame 054095/0268 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Mar 6, 2020
From: LIANG, SIWEI; BAUMANN, THEODORE F.; BIENER, JUERGEN; BIENER, MONIKA M.; MORAN, BRYAN D.; OAKDALE, JAMES; YE, JIANCHAO
To: LAWRENCE LIVERMORE NATIONAL SECURITY, LLC
Reel/Frame 052039/0060 →
Continuity (1)
Related Publication 20200317870A1 · Oct 8, 2020
References Cited (32)
US 20070123628A1 · Shirasaki · 2007 [cited by examiner]
US 20080096987A1 · Podszun · 2008 [cited by examiner]
US 20100233448A1 · Kameyama · 2010 [cited by examiner]
US 20110033663A1 · Svec · 2011 [cited by examiner]
US 20190185328A1 · Humpal · 2019 [cited by examiner]
WO WO2018005501A1 · 2018 [cited by examiner]
WO 2018065094A1 · 2018 [cited by applicant]
Machine translation of CN 104628917A by Lu et al. (Year: 2015). [cited by examiner]
CN 104628917_Scifinder abstract. by Scifinder. Accessed Mar. 16, 2021. (Year: 2015). [cited by examiner]
Larranaga, M.D., Lewis, R.J., Sr. and Lewis, R.A. (2016). R. In Hawley's Condensed Chemical Dictionary, Sixteenth Edition (eds M.D. Larranaga, R.J. Lewis and R.A. Lewis). https://doi.org/10.1002/9781119312468.ch18 (Year… [cited by examiner]
Michael Müller et al 2015 Biofabrication 7 035006 (Year: 2015). [cited by examiner]
Machine Translation of JP H0967307 by Nakamura et al. (Year: 1997). [cited by examiner]
Machine translation of CN 108855229 A (Year: 2018). [cited by examiner]
Rolland et al., “Solvent-Resistant Photocurable “Liquid Teflon” for Microfluidic Device Fabrication,” Journal of the American Chemical Society, vol. 126, 2004, pp. 2322-2323. [cited by applicant]
Williams et al., “High-Resolution PFPE-based Molding Techniques for Nanofabrication of High-Pattern Density, Sub-20 nm Features: A Fundamental Materials Approach,” American Chemical Society, Nano Letters, vol. 10, 2010,… [cited by applicant]
Demarco et al., “A New Perfluoropolyether-Based Hydrophobic and Chemically Resistant Photoresist Structured by Two-Photon Polymerization,” American Chemical Society, Langmuir, vol. 29, 2013, pp. 426-431. [cited by applicant]
Keller et al., “Study of Biofilm Growth on Slippery Liquid-Infused Porous Surfaces Made from Fluoropor,” American Chemical Society, Applied Materials and Interfaces, vol. 11, Jan. 15, 2019, pp. 4480-4487. [cited by applicant]
Helmer et al., “Transparent, abrasion-insensitive superhydrophobic coatings for real-world applications,” Scientific Reports, vol. 7, Nov. 8, 2017, pp. 15078:1-15078:6. [cited by applicant]
Gladysz et al., “Chapter 4: Techniques for Introducing Intentional Voids into Materials,” Voids in Materials, Elsevier B.V., 2015, pp. 49-71. [cited by applicant]
Zheng et al., “Multiscale metallic metamaterials,” Nature Materials, vol. 15, Oct. 2016, pp. 1100-1106. [cited by applicant]
Chen et al., “Preparation of polymer-based porous scaffolds for tissue engineering,” Characterisation and Design of Tissue Scaffolds, Elsevier B.V., 2016, pp. 105-125. [cited by applicant]
Mane S., “Effect of Porogens (Type and Amount) on Polymer Porosity: A Review,” Canadian Chemical Transactions, vol. 2, Issue 2, 2016, pp. 210-225. [cited by applicant]
Hensleigh et al., “Additive manufacturing of complex micro-architected graphene aerogels,” Materials Horizons, vol. 5, No. 6, Nov. 2018, pp. 1035-1041. [cited by applicant]
Mu et al., “Porous polymeric materials by 3D printing of photocurable resin,” Materials Horizons, 2017, pp. 442-449. [cited by applicant]
Zheng et al., “Ultralight, Ultrastiff Mechanical Metamaterials,” Science, vol. 344, Issue 6190, Jun. 20, 2014, pp. 1373-1377. [cited by applicant]
Ge et al., “Multimaterial 4D Printing with Tailorable Shape Memory Polymers,” Scientific Reports, No. 6:31110, Aug. 8, 2016, pp. 1-11. [cited by applicant]
Lewis J., “Direct Ink Writing of 3D Functional Materials,” Advanced Functional Materials, vol. 16, 2006, pp. 2193-2204. [cited by applicant]
Rodriguez et al., “Shape-morphing composites with designed micro-architectures,” Scientific Reports, No. 6:27933, Jun. 15, 2016, pp. 1-10. [cited by applicant]
Zhu et al., “Highly compressible 3D periodic graphene aerogel microlattices,” Nature Communications, No. 6:6962, Apr. 22, 2015, pp. 1-8. [cited by applicant]
Biener et al., “Advanced carbon aerogels for energy applications,” Energy & Enviornmental Science, vol. 4, Feb. 16, 2011, pp. 656-667. [cited by applicant]
Oakdale et al., “Post-print UV curing method for improving the mechanical properties of prototypes derived from two-photon lithography,” Optics Express, vol. 24, No. 24, Nov. 28, 2016, pp. 27077-27086. [cited by applicant]
Duoss et al., “Three-Dimensional Printing of Elastomeric, Cellular Architectures with Negative Stiffness,” Advanced Functional Materials, vol. 24, 2014, pp. 4905-4913. [cited by applicant]