Methods for manufacturing electrodes including fluoropolymer-based solid electrolyte interface layers
Methods for manufacturing electrodes include applying a fluoropolymer film to a lithium-based host material, defluorinating the fluoropolymer film by heating to produce a lithium electrode having a solid electrolyte interface (SEI) layer including defluorinated fluoropolymers and at least about 5 wt. % LiF. The fluoropolymers can include one or more of fluorinated ethylenepropylene, perfluoroalkoxy alkanes, vinylidenefluoride, and copolymers of perfluoromethylvinylether and tetrafluoroethylene. The fluoropolymers can include one or more fluorinated monomers, including hexafluoropropylene, tetrafluoroethylene, ethylene-tetrafluoroethylene, perfluoroethers, and vinylidene fluoride. The —CF 3 functional groups of the defluorinated fluoropolymers can be about 3 wt. % to about 10 wt. % of the SEI layer. The SEI layer can include about 30 wt. % to about 50 wt. % LiF. The method can include assembling a battery cell by disposing a battery separator between a cathode and the electrode, and disposing the battery separator, the cathode, and the electrode in an electrolyte.
1. A method for manufacturing an electrode, the method comprising:
providing an electrode comprising a current collector and a lithium-based host material applied thereto;
applying a fluoropolymer film including one or more fluoropolymers to an exposed surface of the lithium-based host material; and
defluorinating the fluoropolymer film by heating to produce a lithium electrode having a solid electrolyte interface (SEI) layer comprising defluorinated fluoropolymers and at least about 5 wt. % LiF, wherein the heating occurs below the melting point of the lithium-based host material.
2. The method of claim 1 , wherein the one or more fluoropolymers comprise one or more of fluorinated ethylene propylene (FEP), perfluoroalkoxy alkanes (PFA), vinylidene fluoride (THV), and copolymers of perfluoromethylvinylether and tetrafluoroethylene (MFA).
3. The method of claim 1 , wherein the fluoropolymer film comprises one or more fluoropolymers selected from the group consisting of fluorinated ethylene propylene (FEP), perfluoroalkoxy alkanes (PFA), vinylidene fluoride (THV), and copolymers of perfluoromethylvinylether and tetrafluoroethylene (MFA).
4. The method of claim 1 , wherein the one or more fluoropolymers comprise one or more fluorinated monomers, wherein the fluorinated monomers include hexafluoropropylene, tetrafluoroethylene, ethylene-tetrafluoroethylene, perfluoroethers, and vinylidene fluoride.
5. The method of claim 1 , wherein —CF 3 functional groups of the one or more fluoropolymers comprise at least about 10 wt. % of the fluoropolymer film as applied to the lithium-based host material.
6. The method of claim 1 , wherein —CF 3 functional groups of the one or more defluorinated fluoropolymers comprise about 3 wt. % to about 10 wt. % of the SEI layer.
7. The method of claim 1 , wherein the SEI layer comprises about 30 wt. % to about 50 wt. % LiF.
8. The method of claim 1 , wherein the lithium-based host material comprises at least about 50 wt. % lithium.
9. The method of claim 1 , further comprising removing a natural passivation layer from the exposed surface of the lithium-based host material onto which the fluoropolymer film is subsequently applied.
10. A method for manufacturing a battery cell, the method comprising:
providing an anode comprising a current collector and a lithium-based host material applied thereto;
applying a fluoropolymer film including one or more fluoropolymers to a plurality of exposed surfaces of the lithium-based host material;
defluorinating the fluoropolymer film by heating to produce a lithium anode having a solid electrolyte interface (SEI) layer comprising defluorinated fluoropolymers and at least about 5 wt. % LiF, wherein the heating occurs below the melting point of the lithium-based host material; and
subsequently assembling the battery cell by:
disposing a battery separator between a cathode and the lithium anode, and
disposing the battery separator, the cathode, and the lithium anode in an electrolyte.
11. The method of claim 10 , wherein the electrolyte comprises a liquid electrolyte.
12. The method of claim 10 , wherein applying is conducted under a vacuum and/or in an inert atmosphere.
13. The method of claim 10 , wherein the one or more fluoropolymers are applied to the plurality of exposed surfaces of the lithium-based host material via a plasma-based process, and the heating at least partially occurs during the applying.
14. The method of claim 10 , further comprising removing a natural passivation layer from the lithium-based host material prior to applying, wherein the heating that occurs during the applying effects a suitable extent of defluorination of the fluoropolymer film.
15. The method of claim 10 , further comprising, after applying, transporting and/or storing the lithium anode in a non-inert environment prior to defluorinating.
16. The method of claim 15 , wherein the one or more fluoropolymers are applied to the plurality of the exposed surfaces of the lithium-based host material via thermal evaporation or electron beam evaporation.
17. The method of claim 15 , wherein the plurality of exposed surfaces of the lithium-based host material each comprises a passivation layer, and the plurality of passivation layers are not removed prior to applying.
18. The method of claim 10 , wherein —CF 3 functional groups of the one or more fluoropolymers comprise at least about 10 wt. % of the fluoropolymer film as applied to the lithium-based host material.
19. The method of claim 10 , wherein the SEI layer comprises about 30 wt. % to about 50 wt. % LiF.