Brake disk including decarburized layer and nitride compound layer, and method of manufacturing the same
A brake disk includes a basic material formed of gray cast iron, a decarburized layer formed on the basic material and formed via decarburizing, and a nitride compound layer formed on the decarburized layer and formed via nitriding of a nitride. A method of manufacturing a brake disk includes preparing a disk formed of gray cast iron, performing heat treatment of the disk to form a pre-decarburized layer and a base layer of gray cast iron over which the pre-decarburized layer is formed, and nitriding a portion of the pre-decarburized layer to form a nitride compound layer including a nitride and a decarburized layer over which the nitride compound layer is formed.
1. A method of manufacturing a brake disk, the method comprising:
forming a disk with gray cast iron;
performing heat treatment of the disk to form a pre-decarburized layer and a base layer of gray cast iron over which the pre-decarburized layer is formed; and
nitriding a portion of the pre-decarburized layer to form a nitride compound layer including a nitride and a decarburized layer over which the nitride compound layer is formed,
wherein:
the disk comprises the base layer, the decarburized layer formed over the base layer, and the nitride compound layer formed over the decarburized layer,
the disk comprises a basic material of gray cast iron that includes precipitated carbide, and
carbide that remains in the pre-decarburized layer after the performing of the heat treatment has a content equal to or less than 3% based on a total weight of the pre-decarburized layer.
2. The method of claim 1 , wherein the performing of the heat treatment is performed for 15 minutes to 60 minutes at 680° C. to 750° C.
3. The method of claim 1 , wherein the nitriding is performed on the pre-decarburized layer under an atmosphere of reaction gas including ammonia, nitrogen, and carbon dioxide.
4. The method of claim 3 , wherein the reaction gas includes ammonia, nitrogen, and carbon dioxide with a volume ratio of 5 to 7:2 to 4:1.
5. The method of claim 3 , wherein the nitriding is performed for 3 hours to 8 hours at 550° C. to 600° C.
6. A brake disk manufactured by a method comprising the steps of:
forming a disk with gray cast iron;
performing heat treatment of the disk to form a pre-decarburized layer and a base layer of gray cast iron over which the pre-decarburized layer is formed; and
nitriding a portion of the pre-decarburized layer to form a nitride compound layer including a nitride and a decarburized layer over which the nitride compound layer is formed,
wherein:
the disk comprises the base layer, the decarburized layer formed over the base layer, and the nitride compound layer formed over the decarburized layer,
the disk comprises a basic material of gray cast iron that includes precipitated carbide, and
carbide that remains in the pre-decarburized layer after the performing of the heat treatment has a content equal to or less than 3% based on a total weight of the pre-decarburized layer.