Swine-waste biochar as a sustainable cement replacement material
View Patent ↗The presently application relates generally a composition comprising swine waste biochar and cement and methods of making same.
1. A cementitious composition comprising swine waste biochar and cement, wherein the swine waste biochar comprises about 40%-60% carbon, about 25% 45% oxygen, about 2% 11° A phosphorus and about 2%-10% calcium.
2. The cementitious composition of claim 1 , wherein swine waste biochar comprises between about 0.25% and about 30% by weight of the composition.
3. The cementitious composition of claim 2 , wherein said swine waste biochar comprises between about 1% and about 15% by weight of the composition.
4. The cementitious composition of claim 1 , wherein said swine waste biochar comprises about 50-60% carbon and about 25%-35% oxygen.
5. The cementitious composition of claim 1 , wherein said swine waste biochar comprises about 55% carbon, about 30% oxygen, about 5% phosphorus and about 5% calcium.
6. A composition comprising about 1 part by weight cementitious materials, about 1 to about 3 parts by weight fine aggregate, about 1 to about 5 parts by weight coarse aggregate, and about 0.2 to about 0.6 parts by weight water, wherein the cementitious materials comprise about 0.25% to about 30% by weight swine waste biochar and about 99.75% to about 70% by weight cement, wherein the swine waste biochar comprises about 40%-60% carbon, about 25%-45% oxygen, about 2%-11% phosphorus and about 2%-10% calcium.
7. The composition of claim 6 , wherein the fine aggregate is sand and the coarse aggregate is stone.
8. The composition of claim 6 , wherein said swine waste biochar comprises about 50-60% carbon and about 25%-35% oxygen.
9. The composition of claim 6 , wherein said swine waste biochar comprises about 55% carbon, about 30% oxygen, about 5% phosphorus and about 5% calcium.
10. The composition of claim 6 , wherein the cementitious materials comprise about 1% to about 15% by weight swine waste biochar and about 99% to about 85% by weight cement.
11. The composition of claim 10 , wherein the fine aggregate is sand and the coarse aggregate is stone.
12. The composition of claim 10 , wherein said swine waste biochar comprises about 50-60% carbon and about 25%-35% oxygen.
13. The composition of claim 10 , wherein said swine waste biochar comprises about 55% carbon, about 30% oxygen, about 5% phosphorus and about 5% calcium.
14. A method of accelerating the setting of a cement paste comprising combining cement with swine waste biochar to obtain a blended mix before the addition of water.
15. The method of claim 14 , wherein said cement paste has a shorter initial time of setting and/or a shorter final time of setting compared to cement paste that does not contain swine waste biochar.
16. The method of claim 14 , wherein said set cement paste has reduced water absorption compared to cement paste that does not contain swine waste biochar.
17. The method of claim 16 , wherein said water absorption is reduced by at least about 60% compared to water absorption of cement paste that does not contain swine waste biochar.