High separation performance polydialkylsiloxane pervaporation membranes
A pervaporation membrane formed on a porous support containing a composition encompassing a polysiloxane, a crosslinker and a catalyst are disclosed and claimed. Also disclosed are the fabrication of membranes which exhibit unique separation properties, and their use in the separation of organic volatiles from biomass and/or organic waste, including butanol, ethanol, and the like.
1. A method of separating butanol from a feedstock selected from a fermentation broth or a waste comprising:
charging the feedstock to a pervaporation module containing a pervaporation membrane formed by a composition comprising:
i) a polydialkylsiloxane of the formula (I):
where x is an integer from about 100 to 500 such that the number average molecular weight (Mn) is at least about 50,000;
R is selected from the group consisting of methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl and tert-butyl; and
R 1 is selected from the group consisting of hydrogen, methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, tert-butyl, 2-propenyl, diacetoxymethyl, amine and aminomethyl;
ii) a crosslinker selected from the group consisting of methyltriethoxysilane, and vinyltris(methylethyl-ketoximino)silane; and
iii) a catalyst selected from the group consisting of tetrakis(trimethylsiloxy)titanium, titanium di-n-butoxide bis(2,4-pentanedionate), titanium diisopropoxide bis(2,4-pentanedionate), titanium diisopropoxide bis(ethylacetoacetate) and dibutyltin dilaurate; and
collecting a permeate vapor containing butanol from the pervaporation module; wherein said pervaporation module exhibits a flux for butanol of at least about 500 g/m 2 /hr, and wherein the concentration of butanol in the feedstock is 1 weight percent or higher.
2. The method according to claim 1 , wherein the fermentation broth is charged to the pervaporation module at a temperature from about 60° C. to about 110° C.
3. The method according to claim 1 , wherein a vacuum from about 0.1 in Hg to about 25 in Hg is applied to the pervaporation module.
4. The method according to claim 1 , wherein the pervaporation membrane is formed by a polydialkylsiloxane of the formula (I) where:
R is selected from the group consisting of methyl and ethyl; and
R 1 is selected from the group consisting of hydrogen, methyl, ethyl, 2-propenyl, diacetoxymethyl, amine and aminomethyl.
5. The method according to claim 1 , wherein the pervaporation membrane is formed by a polydialkylsiloxane of the formula (I) where:
R is methyl; and
R 1 is selected from the group consisting of hydrogen and 2-propenyl.