Films and laminates for use in packaging reactive compounds
The present present disclosure relates to a laminate film including a water resistant or oxygen resistant base layer, and co-extrusion layer. The coextrusion layer may include a tie layer and a contact layer, and the contact layer may include a polymer such as cyclic olefin copolymer, a polyamide, or an ethylene vinyl alcohol. A total loading of the tie layer may be in the range of 3-9 g/m 2 and wherein a loading of the contact layer is: loading contact =x*loading tie , wherein loading contact is the loading of the contact layer, loading tie is the total loading of the tie layer, and x is in the range of 0.8 to 3.
1. An aggressive chemical-resistant laminate film comprising:
a base layer, wherein the base layer is one or more of water or oxygen resistant; and
a co-extrusion layer, the co-extrusion layer comprising a tie layer and a contact layer, wherein the contact layer comprises a polymer selected from the group consisting of a cyclic olefin copolymer, a polyamide, an ethylene vinyl alcohol, or a combination thereof;
wherein a total loading of the tie layer is in the range of 3-9 g/m2 and wherein a loading of the contact layer is:
loadingcontact=x*loadingtie, wherein loadingcontact is the loading of the contact layer, loadingtie is the total loading of the tie layer, and x is in the range of 1 to 3, wherein the aggressive chemical-resistant laminate film is resistant to a chemical selected from nicotine, fentanyl, rivastigmine, or lidocaine.
2. The laminate film according to claim 1 , wherein x is in the range of 1.33 to 2.75.
3. The laminate film according to claim 1 , wherein the tie layer is a multilayered tie layer comprising at least two layers.
4. The laminate film according to claim 3 , wherein at least one layer of Flail the multilayered tie layer is made from a material selected from the group consisting of: ethylene methacrylic acid, ethylene acrylic acid, a terpolymer of ethylene, acrylic ester, and maleic anhydride, a terpolymer of ethylene, butyl acrylate, and maleic anhydride, or combinations thereof.
5. The laminate film according to claim 3 , wherein a second layer of the multilayered tie layer comprises a material selected from the group consisting of ethylene methacrylic acid, low-density polyethylene, ethylene methyl acrylate, ethylene butyl acrylate, ethylene ethyl acrylate, a terpolymer of ethylene, acrylic ester, and maleic anhydride, a terpolymer of ethylene, butyl acrylate, and maleic anhydride, ethylene acrylic acid, or combinations thereof.
6. The laminate film according to claim 1 , wherein the tie layer consists of two layers, a first tie layer and a second tie layer.
7. The laminate film according to claim 6 , wherein a loading ratio of the first tie layer to the second tie layer is approximately 1:1.
8. The laminate film according to claim 1 , wherein the base layer is selected from the group consisting of a metal foil and a polymer made of a polyamide, silicon, aluminiumoxide coated polyesters and fluoropolymers, or a combination thereof.