Steel part
A formed steel part includes a first steel plate having a first base, a first intermetallic alloy layer on the first base and a first metal alloy layer on the first intermetallic alloy layer, the first steel part having a first area without the first metal alloy layer and having at least part of the first intermetallic alloy layer; and a second steel plate having a second base, a second intermetallic alloy layer on the second base and a second metal alloy layer on the second intermetallic alloy layer, the second steel part having a second area without the second metal alloy layer and having at least part of the second intermetallic alloy layer in the second area. The first and second steel plates are joined together. The formed steel part may also include a butt-weld joining the first and second steel plates.
1. A welded blank comprising:
a first steel plate having a first base, a first intermetallic alloy layer on the first base and a first metal alloy layer on the first intermetallic alloy layer; and
a second steel plate having a second base, a second intermetallic alloy layer on the second base and a second metal alloy layer on the second intermetallic alloy layer;
the first and second steel plates being butt-welded together at a weld, the weld including material from at least the first base, the first intermetallic alloy layer, the second base and the second intermetallic layer and capable of forming a welded joint after heat treatment and quenching of being totally martensitic and free of intermetallic areas.
2. The welded blank as recited in claim 1 , wherein after said heat treatment and quenching, the first and second intermetallic layers are alloyed to the first and second bases.
3. The welded blank as recited in claim 1 wherein, after said heat treatment and quenching, the welded blank is corrosion resistant at the weld.
4. The welded blank as recited in claim 1 wherein, after said heat treatment and quenching, the welded blank has a tensile strength greater than 1450 MPa.
5. The welded blank as recited in claim 1 wherein, after said heat treatment and quenching, the welded blank has an elongation in a crosswise direction of above 4%.
6. The welded blank as recited in claim 1 wherein the first and second metal alloy layers comprise aluminum and, by weight:
from 8 to 11% silicon; and
from 2 to 4% iron.
7. The welded blank as recited in claim 1 wherein the first and second steel plates are from 1 to 3 mm thick.
8. The welded blank as recited in claim 1 wherein the first and second steel plates have different thicknesses.
9. The welded blank as recited in claim 1 , wherein the composition of the first and second bases comprise, by weight: 0.10%≤C≤0.5%, 0.5%≤Mn≤3%, 0.1%≤Si≤1%, 0.01%≤Cr≤1%, Ti≤0.2%, Al≤0.1%, S≤0.05%, P≤0.1%, 0.0005%≤B≤0.010%, the remainder consisting of iron and inevitable impurities resulting from the production process.
10. The welded blank as recited in claim 9 , wherein the composition of the first and second bases comprise, by weight: 0.15%≤C≤0.25%, 0.8%≤Mn≤1.8%, 0.1%≤Si≤0.35%, 0.01%≤Cr≤0.5%, Ti≤0.1%, Al≤0.1%, S≤0.05%, P≤0.1%, 0.002%≤B≤0.005%, the remainder consisting of iron and inevitable impurities produced by the production process.
11. The welded blank as recited in claim 1 , wherein after said heat treatment and quenching, the welded blank has a tensile strength between about 1250 and about 1650 MPa.
12. The welded blank as recited in claim 1 , wherein the weld is obtained by laser beam welding.
13. The welded blank as recited in claim 1 , wherein the weld is obtained by electric arc welding.
14. The welded blank as recited in claim 1 wherein, after said heat treatment and quenching, the welded blank has an elongation in a crosswise direction ≥4%.
15. The welded blank as recited in claim 1 wherein, after said heat treatment and quenching, the welded blank is corrosion resistant in areas adjacent the weld.
16. The welded blank as recited in claim 1 wherein the first and second steel parts are butt-welded at respective first and second edges of the first and second steel parts, and wherein, after said heat treatment and quenching, the welded blank is corrosion resistant at an area of the first steel part extending 0.2 mm from the first edge and at an area of the second steel part extending 0.2 mm from the second edge.
17. The welded blank as recited in claim 1 wherein the first and second steel parts are butt-welded at respective first and second edges of the first and second steel parts, and wherein, after said heat treatment and quenching, the welded blank is corrosion resistant at an area of the first steel part extending 2 mm from the first edge and at an area of the second steel part extending 2 mm from the second edge.
18. The welded blank as recited in claim 1 , wherein the first and second intermetallic alloy layers each comprise iron and aluminum.
19. The welded blank as recited in claim 1 , wherein a thickness of the each of the first and second intermetallic layers is between 3 and 10 micrometers.
20. A welded blank comprising:
a first steel plate having a first base, a first intermetallic alloy layer on the first base and a first metal alloy layer on the first intermetallic alloy layer; and
a second steel plate having a second base, a second intermetallic alloy layer on the second base and a second metal alloy layer on the second intermetallic alloy layer;
the first and second steel plates being butt-welded together at a weld, the weld including material from at least the first base, the first intermetallic alloy layer, the second base and the second intermetallic layer, and capable of forming a welded joint after heat treatment and quenching the weld being totally martensitic and having an elongation in a crosswise direction ≥4%.
21. The welded blank as recited in claim 20 , wherein the first and second intermetallic layers include iron and aluminum, and wherein after said heat treatment and quenching, the first and second intermetallic layers are alloyed to the first and second bases.
22. The welded blank as recited in claim 20 wherein, after said heat treatment and quenching, the welded blank has a tensile strength greater than 1450 MPa.
23. The welded blank as recited in claim 20 wherein, after said heat treatment and quenching, the welded blank has an elongation in a crosswise direction of above 4%.
24. The welded blank as recited in claim 20 wherein the first and second metal alloy layers comprise aluminum and, by weight:
from 8 to 11% silicon; and
from 2 to 4% iron.
25. The welded blank as recited in claim 20 wherein the first and second steel plates have different thicknesses.
26. The welded blank as recited in claim 20 , wherein the composition of the first and second bases comprise, by weight: 0.10%≤C≤0.5%, 0.5%≤Mn≤3%, 0.1%≤Si≤1%, 0.01%≤Cr≤1%, Ti≤0.2%, Al≤0.1%, S≤0.05%, P≤0.1%, 0.0005%≤B≤0.010%, the remainder consisting of iron and inevitable impurities resulting from the production process.
27. A welded blank the welded blank has a tensile strength between about 1250 and about 1650 MPa.
28. The welded blank as recited in claim 20 , wherein the weld is obtained by laser beam welding or by electric arc welding.
29. The welded blank as recited in claim 20 wherein, after said heat treatment and quenching, the welded blank is corrosion resistant in areas adjacent the weld.
30. The welded blank as recited in claim 20 , wherein a thickness of each of the first and second intermetallic layers is between 3 and 10 micrometers.