Materials and methods for components of lithium batteries
The present invention relates to materials and methods for components of lithium batteries, such as metal anodes having a protective coating.
1. A metal anode having a protective coating comprising:
a metal layer consisting of lithium, sodium, or potassium, wherein the metal layer has first major surface and a second major surface; and
a conformal protective coating on the first major surface of the metal layer, wherein the conformal protective coating comprises a composite material, wherein the composite material comprises; and
a current collector on the second major surface of the metal layer.
2. The metal anode of claim 1 , wherein the composite material comprises (a) a lithium oxide-containing material when the metal layer comprises lithium; (b) a sodium oxide-containing material when the metal layer comprises sodium; or (c) a potassium oxide-containing material when the metal layer comprises potassium.
3. The metal anode of claim 2 , wherein the composite material comprises (a) Li 2 O—Li 2 CO 3 , Li 2 O—LiF, Li 2 O—LiBF 4 , or any combination of these materials when the metal layer comprises lithium; (b) Na 2 O—Na 2 CO 3 , Na 2 O—NaF, Na 2 O—NaBF 4 , or any combination of these materials when the metal layer comprises sodium, and (c) K 2 O—K 2 CO 3 , K 2 O—KF, K 2 O—KBF 4 , or any combination of these materials when the metal layer comprises potassium.
4. A metal anode having a protective coating comprising:
a metal layer consisting of lithium, sodium, or potassium, wherein the metal layer has first and second major surfaces; and
a protective coating on the first major surface of the metal layer, wherein the protective coating comprises a composite material, wherein the composite material comprises M x HfO 2 , where X≥1 and M is Li, Na, K, or a mixture thereof, and
a current collector on the second major surface of the metal layer.
5. The metal anode of claim 4 , wherein the metal layer of the metal anode has a thickness of 10 μm to 150 μm.
6. The metal anode of claim 4 , wherein the protective coating has a thickness from 1 nm to 10 microns.
7. The metal anode of claim 4 , wherein the protective coating is formed on the metal layer by atomic layer deposition, plasma enhanced atomic layer deposition, chemical vapor deposition, plasma enhanced chemical vapor deposition, sputtering, physical vapor deposition, spinning coating, dip coating, or pulsed laser deposition.
8. The metal anode of claim 1 , wherein the composite material comprises lithium fluoride (LiF).
9. The metal anode of claim 8 , wherein the composite material comprises LiF—Li 2 CO 3 .
10. The metal anode of claim 1 , wherein the metal layer of the metal anode has a thickness of 10 μm to 150 μm.
11. The metal anode of claim 1 , wherein the conformal protective coating has a thickness from 1 nm to 10 microns.
12. The metal anode of claim 1 , wherein the conformal protective coating is formed on the metal layer by atomic layer deposition, plasma enhanced atomic layer deposition, chemical vapor deposition, plasma enhanced chemical vapor deposition, sputtering, physical vapor deposition, spinning coating, dip coating, or pulsed laser deposition.
13. The metal anode of claim 2 , wherein the composite material comprises lithium carbonate (Li 2 CO 3 ).
14. The metal anode of claim 1 , wherein the composite material comprises lithium hexafluorophosphate (LiPF 6 ).
15. The metal anode of claim 1 , wherein the composite material comprises lithium tetrafluoroborate (LiBF 4 ).
16. The metal anode of claim 1 , wherein the conformal protective coating is formed on the metal layer by reacting or decomposing a first coating material precursor on the metal layer, and reacting or decomposing a second coating material precursor on the first coating material precursor.
17. The metal anode of claim 4 , wherein the protective coating is formed on the metal layer by reacting or decomposing a first coating material precursor on the metal layer, and reacting or decomposing a second coating material precursor on the first coating material precursor.
18. The metal anode of claim 1 , wherein the composite material further comprises lithium fluoride-lithium oxide (LiF—Li 2 O), lithium fluoride-lithium carbonate (LiF—Li 2 CO 3 ), lithium fluoride-lithium hexafluorophosphate (LiF—LiPF 6 ), lithium fluoride-lithium tetrafluoroborate (LiF—LiBF 4 ), Li 2 O—Li 2 CO 3 , Li 2 O—LiF, Li 2 O—LiBF 4 , LiF—NbO 2 , Li 3 N—AlN, LixSi 3 N 4 , Li x Nb 3 N 4 , where X≥0 or any combination of these materials.
19. The metal anode of claim 5 , wherein the composite material further comprises MF-M 2 O, MF-M 2 CO 3 , MF-MPF 6 , MF-MBF 4 , MF-NbO 2 , M 2 O-M 2 CO 3 , M 2 O-MBF 4 , M 3 N—AlN, M 3 N—AlN, M x Si 3 N 4 , M x Nb 3 N 4 , or any combination thereof.