Fiber cement product comprising at least one profiled surface

1. A method for increasing hydrophobicity of a fiber cement product, said method comprising the steps of

providing a fiber cement product comprising at least one profiled surface where grooves are milled, said grooves each having a depth in the range 0.15 mm to 1 mm and a maximum width at a bottom of the groove in the range 2 mm to 20 mm; and

applying a hydrophobation agent to the at least one profiled surface

to obtain fiber cement product having a water take up of less than 1.5 mL after 48 hours as measured by the RILEM Test No 11.4 in horizontal application,

wherein the hydrophobation agent is water free and the combination of a silane-based liquid comprising at least one silane of the formula SiR 4 with each of the four R-groups independently being an organic group, three of the R-groups being selected from ethoxy or methoxy groups and the fourth R-group being a branched or linear hydrocarbon chain of an octyl, isobutyl or methyl group, and at least one oligomer siloxane of the formula H(R 2 SiO) n OH with each of the R-groups independently being an organic group; and

allowing said silane-based liquid to penetrate the at least one profiled surface without leaving visual traces.

2. A method according to claim 1 , wherein the water take up is less than 1 mL per 48 hours.

3. A method according to claim 1 , wherein the fiber cement product is a fiber cement plate.

4. A method according to claim 1 , wherein the grooves are equally distributed over said surface, said grooves all have a uniform direction and a uniform depth.

5. A method according to claim 1 , wherein each said groove has a trapezoid cross section in a section according to a plane perpendicular to the direction of the groove, said groove having a flat bottom and two flanks, the angles between the bottom and each of said flanks is in the range of 90° to about 180.

6. A method according to claim 1 , comprising the step of autoclave curing the fiber cement product.

7. A method according to claim 1 , comprising the step of air curing the fiber cement product.

8. A method according to claim 1 , wherein the provision of a fiber cement product comprising at least one profiled surface comprises providing a green fiber cement plate using a Hatschek process, and profiling at least one surface of said fiber cement plate.

9. A method according to claim 8 , wherein the green fiber cement plate is cured using autoclave curing.

10. A method according to claim 8 , wherein the green fiber cement plate is cured using air curing.

11. A method according to claim 8 , wherein the at least one profiled surface is provided by profiling a surface of the green fiber cement product.

12. A method according to claim 8 , wherein the at least one profiled surface is a post-curing profiled surface.

13. A method according to claim 12 , wherein the at least one profiled surface is provided by milling the fiber cement product.

14. A method according to claim 1 , wherein the hydrophobation agent is applied to the at least one profiled surface by spraying.

15. A method according to claim 14 , comprising the additional step of

changing angular orientation of spray nozzles to ensure an amount of hydrophobation agent is uniformly sprayed over the at least one profiled surface and reaches corners thereof.

16. A method according to claim 1 , wherein the silane-based liquid comprises at least 50% w of the at least one silane.

17. A method according to claim 1 , wherein said grooves are milled to a depth 0.15 mm to 0.5 mm, and maximum width of 4 mm to 15 mm.

18. A method according to claim 1 , wherein the hydrophobation agent is also solvent-free.

19. A fiber cement product obtained according to claim 1 .

20. A fiber cement product according to claim 19 , wherein the at least one profiled surface is free of silane- and siloxane-residue.