Conductive polymer nanowires—graphene hybrids with improved optoelectronic properties
A photodetector including graphene and poly(3-hexylthiopene) (P3HT) nanowires is claimed. A method of making the hybrid photodetector is also claimed.
1. A hybrid photodetector comprising atomically thin graphene and a conductive polymer wherein the conductive polymer is poly (3-hexylthiophene) (P3HT) nanowires self-assembled from regioregular P3HT and a mesh-like mesostructure is formed on top of the atomically thin graphene with voids between nanowires in the range of the wavelength of light.
2. The photodetector of claim 1 , wherein the P3HT nanowires are about 2-4 μm in length.
3. The photodetector of claim 1 , wherein the photodetector comprises no planar P3HT thin film.
4. The photodetector of claim 1 , wherein the graphene has a thickness of about 0.33 nm.
5. The photodetector of claim 1 , wherein the graphene has a thickness of 0.33 nm and the P3HT nanowires have a thickness of 11 nm.
6. A method of making a hybrid photodetector comprising (1) providing regioregular poly (3-hexylthiophene) (P3HT) and atomically thin graphene; (2) either using a Whiskers method or a mixed solvent method to make the regioregular P3HT self-assemble into P3HT nanowires; and (3) either dropping or spin-casting the P3HT nanowires onto the graphene to form a conductive nanowire mesh hybrid photodetector.
7. The method of claim 6 , wherein the mixed solvent method is used and the solvents are chlorobenzene and acetone.
8. The method of claim 7 , wherein the regioregular P3HT is dissolved in chlorobenzene to form a solution then heated for at least 3 hours; acetone is added to the solution with stirring to form a mixed solution; and the mixed solution is stirred and heated for at least 10 hours then cooled to room temperature.
9. The method of claim 8 , wherein the ratio of chlorobenzene to acetone is about 3:1.
10. The method of claim 8 , wherein the solution is heated to about 95° C. and the mixed solution is heated to about 90° C.
11. The method of claim 7 , wherein the P3HT nanowires are present in the solvents in a concentration of about 0.5 to about 2.5 mg/ml.
12. The method of claim 6 , wherein spin-casting is used and the spin-casting occurs at about 1500 rpm to about 2500 rpm.