Low firing temperature dielectric materials designed to be co-fired with high bismuth garnet ferrites for miniaturized isolators and circulators
Disclosed herein are embodiments of low temperature co-fireable dielectric materials which can be used in conjunction with high dielectric materials to form composite structures, in particular for isolators and circulators for radiofrequency components. Embodiments of the low temperature co-fireable dielectric materials can be scheelite or garnet structures, for example, bismuth vanadate. Adhesives and/or glue is not necessary for the formation of the isolators and circulators.
1. A composite material for use as a radiofrequency component comprising:
a low temperature fireable outer material, the low temperature fireable outer material having a garnet or scheelite structure; and
a high dielectric constant inner material located within the outer material, the high dielectric constant inner material having a dielectric constant above 30, the low temperature fireable outer material and the high dielectric constant inner material being configured to be co-fired together at a temperature between 650-900° C. to form an integrated magnetic/dielectric assembly without the use of adhesive or glue.
2. The composite material of claim 1 wherein the low temperature fireable outer material includes BiVO 4 .
3. The composite material of claim 1 wherein the high dielectric constant inner material is shaped like a disc and the low temperature fireable outer material is shaped like a ring.
4. The composite material of claim 1 wherein the low temperature fireable outer material includes a combination of BiVO 4 and Al 2 O 3 .
5. The composite material of claim 4 wherein the low temperature fireable outer material has a dielectric constant between 20 and 80.
6. The composite material of claim 4 wherein the Al 2 O 3 is present in the low temperature fireable outer material an amount up to about 6 wt %.
7. The composite material of claim 4 wherein Bi 4 V 2 O 11 is present in the low temperature fireable outer material as a phase separate from the BiVO 4 .
8. The composite material of claim 4 wherein the low temperature fireable outer material further includes one or more of yttrium vanadate, gadolinium vanadate, or titanium oxide.
9. The composite material of claim 4 wherein the low temperature fireable outer material further includes titanium oxide in an amount up to 10 wt %.
10. The composite material of claim 8 wherein one or both of yttrium vanadate, gadolinium vanadate form a solid solution with the BiVO 4 in the low temperature fireable outer material.
11. The composite material of claim 4 wherein the low temperature fireable outer material further includes titanium dioxide as a phase separate from the BiVO 4 .
12. The composite material of claim 4 wherein the low temperature fireable outer material further includes gadolinium vanadate in an amount up to 50 wt %.
13. The composite material of claim 8 wherein Bi 4 V 2 O 11 and BiVO 4 are present in the low temperature fireable outer material as separate phases.
14. The composite material of claim 13 wherein Bi 4 V 2 O 11 , BiVO 4 , and Bi 2 Ti 4 O 11 are present in the low temperature fireable outer material as separate phases.
15. The composite material of claim 14 wherein Bi 4 V 2 O 11 , BiVO 4 , Bi 2 Ti 4 O 11 , and TiO 2 are present in the low temperature fireable outer material as separate phases.
16. The composite material of claim 8 wherein Bi 4 V 2 O 11 and GdVO 4 are present in the low temperature fireable outer material as separate phases.