COMPOSITION AND METHOD FOR TREATING AN ASPHALT PAVEMENT WITH A VOID-FILLING ASPHALT EMULSION
A void filling asphalt emulsion and a method of using the void filling asphalt emulsion to fill voids below the surface of an asphalt pavement. The void filling emulsion is prepared by forming a base asphalt emulsion having about 45 to 75 wt. % of an asphalt content, and combining the base asphalt emulsion with a surface tension reducing solution to produce a void filling asphalt emulsion that has about 25 to 50 wt. % of an asphalt content. When applied to an asphalt pavement the void filling emulsion penetrates into the asphalt pavement and fills voids in the asphalt pavement. The void filling emulation further being water resistant so as not to be washed off a pavement surface by water after being applied to the pavement.
1 . A method of preparing a void filling asphalt emulsion, comprising:
providing a base asphalt emulsion having about 45 to about 75 wt. % of an asphalt; and
combining the base asphalt emulsion with a wetting agent solution to produce a void filling asphalt emulsion, wherein the asphalt comprises about 25 to about 50 wt. % of the void filling asphalt emulsion.
2 . The method of claim 1 , wherein the asphalt comprises about 30 to about 45 wt. % of the void filling asphalt emulsion.
3 . The method of claim 1 , wherein the asphalt comprises about 38 to about 44 wt. % of the void filling asphalt emulsion.
4 . The method according to claim 1 , wherein the base asphalt emulsion comprises water and at least one primary emulsifier.
5 . The method of claim 4 , wherein the primary emulsifier comprises at least one of a tall oil based carboxylate or an alkyl amine.
6 . The method according to claim 1 , wherein the wetting agent solution comprises water and at least one surfactant.
7 . The method according to claim 1 , wherein the wetting agent solution comprises at least one of a polymeric surfactant or a mixed stream surfactant.
8 . The method according to claim 1 , wherein the wetting agent solution comprises at least one of an alcohol ethoxylate, an amine ethoxylate, an acetylenic diol ethoxylate, or a propoxylate.
9 . The method according to claim 1 , wherein wetting agent solution comprises at least one of an ethoxysulfate, a sulfate, a sulfonate, a diamine, a fatty acid, an ether, a hydroxythioether, a siloxane, a fluorosurfactant, a quaternary salt, a betains, or a carboxylate.
10 . The method according to claim 1 , wherein the void filling asphalt emulsion comprises about 0.1 to about 3 wt. % of a surfactant based on the total weight of the void filling asphalt emulsion.
11 - 60 . (canceled)
61 . An emulsion comprising:
water;
about 25 to about 50 wt. % of an asphalt; and
at least one emulsifier.
62 . The emulsion of claim 61 , wherein the asphalt comprises about 30 to about 45 wt. % of the emulsion.
63 . The emulsion of claim 61 , wherein the asphalt comprises about 38 to about 44 wt. % of the emulsion.
64 . The emulsion of claim 61 , further comprising at least one surfactant.
65 . The emulsion of claim 61 , wherein the emulsion exhibits a penetration value of at least 80 wt. % within 5 minutes when passing the emulsion through a #500 mesh sieve at 50° C.
66 . The emulsion of claim 65 , wherein the emulsion exhibits a penetration value of at least 85 wt. %.
67 . The emulsion of claim 65 , wherein the emulsion exhibits a penetration value of at least 90 wt. %.
68 . The emulsion of claim 65 , wherein the emulsion exhibits a penetration value of at least 95 wt. %.
69 . The emulsion of claim 65 , wherein the emulsion exhibits a penetration value of about 90 to about 99.9 wt. %.
70 . The emulsion of claim 61 , characterized in that at least a portion of the emulsion is capable of penetrating into below-surface voids of an asphalt after application to the asphalt's surface.
71 - 98 . (canceled)