Light reflective coating for audio product and preparation method thereof
View Patent ↗A light reflective coating for an audio product, including the following parts by weight of constituents: 15-35 parts by weight of resin, 15-35 parts by weight of glass beads, 20-40 parts by weight of aluminum beads, 5-15 parts by weight of a solidifying agent, 10-25 parts by weight of a solvent and 1-8 parts by weight of an additive. The present invention further includes a method for preparing the light reflective coating for an audio product, adopts organic macromolecular materials having good comprehensive performances to perform optimization and combination, and improves the light reflective performance of the combination. The coating prepared with the method of the present invention has a flat, fine and smooth surface, has good gloss retention, and can satisfy the use requirements of an audio product coating for anti-corrosion, anti-weathering and the like.
1. A light reflective coating for an audio product, comprising the following parts by weight of constituents: 15-35 parts by weight of resin, 15-35 parts by weight of glass beads, 20-40 parts by weight of aluminum beads, 5-15 parts by weight of a solidifying agent, 10-25 parts by weight of a solvent and 1-8 parts by weight of an additive.
2. The light reflective coating for an audio product according to claim 1 , wherein the solvent is a mixture of n-butyl acetate and dimethylbenzene.
3. The light reflective coating for an audio product according to claim 2 , wherein the parts by weight of the n-butyl acetate and the dimethylbenzene are respectively 15-20 parts by weight and 3-8 parts by weight.
4. The light reflective coating for an audio product according to claim 1 , wherein the additive is a mixture of a suspending agent, a dispersing agent, a leveling agent and a catalyst.
5. The light reflective coating for an audio product according to claim 4 , wherein the parts by weight of the suspending agent, the dispersing agent, the leveling agent and the catalyst are respectively 1-5 parts by weight, 0.2-2 parts by weight, 0.2-2 parts by weight and 0.1-0.5 parts by weight.
6. The light reflective coating for an audio product according to claim 1 , wherein the resin is amino epoxy resin or acrylic resin.
7. The light reflective coating for an audio product according to claim 1 , wherein the solidifying agent is an organic amine solidifying agent or a polyurethane solidifying agent.
8. The light reflective coating for an audio product according to claim 4 , wherein the suspending agent is fumed silicon dioxide; the dispersing agent is a polyester dispersing agent; the leveling agent is an organic silicon compound; and the catalyst is organic tin.
9. A method for preparing the light reflective coating for an audio product according to claim 1 , comprising the following steps:
adding a first portion of the solvent, the resin, and the additive,
stirring until uniform,
sequentially adding the aluminum beads, the glass beads and a second portion of the solvent,
stirring again until uniform,
sequentially adding the solidifying agent and the remaining solvent, and
stirring until uniform to obtain the light reflective coating for an audio product.