Ultra-high dielectric constant garnet
Disclosed are embodiments of synthetic garnet materials for use in radiofrequency applications. In some embodiments, increased amounts of bismuth can be added into specific sites in the crystal structure of the synthetic garnet in order to boost certain properties, such as the dielectric constant and magnetization. Accordingly, embodiments of the disclosed materials can be used in high frequency applications, such as in base station antennas.
1. A ceramic material configured for radiofrequency applications, the ceramic material comprising:
a yttrium iron garnet crystal structure;
bismuth substituted into the crystal structure for at least some of the yttrium;
praseodymium, neodymium, samarium, dysprosium, ytterbium, or holmium substituted into the crystal structure for at least some of the yttrium; and
Ca or Zr substituted into the crystal structure for at least some of the yttrium.
2. The ceramic material of claim 1 wherein both calcium and zirconium are substituted into the crystal structure for at least some of the yttrium.
3. The ceramic material of claim 1 wherein praseodymium is substituted into the crystal structure.
4. The ceramic material of claim 1 wherein neodymium is substituted into the crystal structure.
5. The ceramic material of claim 1 wherein samarium is substituted into the crystal structure.
6. The ceramic material of claim 1 wherein dysprosium is substituted into the crystal structure.
7. The ceramic material of claim 1 wherein ytterbium is substituted into the crystal structure.
8. The ceramic material of claim 1 wherein holmium is substituted into the crystal structure.
9. The ceramic material of claim 1 wherein the ceramic material has a dielectric constant of at least 31.
10. The ceramic material of claim 1 wherein the ceramic material has a dielectric constant of at least 36.
11. The ceramic material of claim 1 wherein the ceramic material does not include sillenite.
12. A method of manufacturing a ceramic material, the method comprising:
providing a yttrium iron garnet crystal structure;
substituting bismuth into the crystal structure for at least some of the yttrium;
substituting praseodymium, neodymium, samarium, dysprosium, ytterbium, or holmium into the crystal structure for at least some of the yttrium; and
substituting Ca or Zr into the crystal structure for at least some of the yttrium.
13. The method of claim 12 wherein the ceramic material has a dielectric constant of at least 31.
14. The method of claim 12 wherein both calcium and zirconium are substituted into the crystal structure for at least some of the yttrium.
15. A radiofrequency device comprising:
a component formed from a ceramic having a yttrium iron garnet crystal structure;
bismuth substituting into the crystal structure for at least some of the yttrium;
praseodymium, neodymium, samarium, dysprosium, ytterbium, or holmium substituting into the crystal structure for at least some of the yttrium; and
Ca or Zr substituting into the crystal structure for at least some of the yttrium.
16. The radiofrequency device of claim 15 wherein the component is an antenna.
17. The radiofrequency device of claim 15 wherein the component is a circuit board.
18. The radiofrequency device of claim 15 wherein the ceramic has a dielectric constant of at least 31.
19. The radiofrequency device of claim 15 wherein both calcium and zirconium are substituted into the crystal structure for at least some of the yttrium.
20. The method of manufacturing of claim 12 wherein the ceramic material has a dielectric constant of at least 36.
21. The radio frequency device of claim 15 wherein the ceramic does not include sillenite.
22. The radio frequency device of claim 15 wherein the ceramic has a dielectric constant of at least 36.