Compositions and methods for curing concrete
A composition that may be used to retain moisture within fresh concrete as it cures to optimize the curing of the concrete may include one or more hardening and densifying agents (e.g., alkali metal polysilicate, colloidal silica, etc.) and one or more temporary moisture sealing agents (e.g., a wax, etc.). Additionally, such a composition may include a siliconate (e.g., a metal siliconate, such as an alkali metal siliconate like potassium methyl siliconate, etc.). The hardening and densifying agent of such a composition may penetrate the surface of fresh concrete to react with free lime, providing the fresh concrete with a strong surface. The temporary moisture sealing agent may form a moisture barrier on the surface of the fresh concrete to prevent moisture from escaping from the fresh concrete (e.g., evaporating, etc.) before the fresh concrete has sufficiently cured. The temporary moisture sealing agent may degrade within a matter of days (e.g., three days, seven days, 14 days, less than a month, etc.), facilitating its removal from the surface of the concrete once the concrete has cured and enabling further treatment of the surface without undue delay.
1. A method for curing concrete, comprising:
applying at least one hardening and densifying agent and a temporary moisture sealing agent to a surface of fresh concrete, the temporary moisture sealing agent remaining substantially on the surface of the fresh concrete;
curing the fresh concrete with the temporary moisture sealing agent on the surface and holding water within the fresh concrete; and
reacting one or more materials of the at least one hardening and densifying agent with free lime at or near the surface of the fresh concrete to provide a hardened and densified surface.
2. The method of claim 1 , wherein applying the at least one hardening and densifying agent and the temporary moisture sealing agent to the surface of the fresh concrete comprises applying the at least one hardening and densifying agent to the surface and applying the temporary moisture sealing agent to the surface substantially concurrently.
3. The method of claim 1 , further comprising:
removing the temporary moisture sealing agent from the surface of the fresh concrete.
4. The method of claim 3 , wherein the temporary moisture sealing agent is capable of breaking down to facilitate its removal from the surface.
5. The method of claim 3 , wherein removing the temporary moisture sealing agent from the surface of the fresh concrete comprises at least one of brushing the temporary moisture sealing agent from the surface of the fresh concrete and spraying the temporary moisture sealing agent from the surface of the fresh concrete.
6. The method of claim 1 , wherein applying comprises applying the at least one hardening and densifying agent and/or the temporary moisture sealing agent to the surface of the fresh concrete while the surface is wet.
7. A method for curing concrete, comprising:
applying at least one hardening and densifying agent to a surface of fresh concrete; and
applying at least one temporary moisture sealing agent to the surface while the at least one hardening and densifying agent is on the surface, the at least one temporary moisture sealing agent forming a film on the surface of the fresh concrete while remaining substantially on the surface of the fresh concrete.
8. The method of claim 7 , wherein, after applying the at least one temporary moisture sealing agent to the surface, the at least one temporary moisture sealing agent hardens or cures without substantially entering into pores in the surface.
9. The method of claim 7 , wherein applying the at least one temporary moisture sealing agent to the surface comprises applying to the surface at least one temporary moisture sealing agent capable of breaking down to facilitate its removal from the surface.
10. The method of claim 7 , wherein applying the at least one hardening and densifying agent to the surface comprises applying the at least one hardening and densifying agent to the surface in a manner that enables the at least one hardening and densifying agent to enter into pores of the fresh concrete.
11. The method of claim 7 , wherein applying the at least one hardening and densifying agent comprises applying the at least one hardening and densifying agent to the surface of the fresh concrete while the surface is wet.
12. The method of claim 7 , wherein applying the at least one temporary moisture sealing agent comprises applying the at least one temporary moisture sealing agent to the surface of the fresh concrete while the surface is wet.
13. The method of claim 7 , further comprising:
removing the at least one temporary moisture sealing agent from the surface of the fresh concrete.
14. The method of claim 12 , wherein removing the temporary moisture sealing agent from the surface of the fresh concrete comprises at least one of brushing the temporary moisture sealing agent from the surface of the fresh concrete and spraying the temporary moisture sealing agent from the surface of the fresh concrete.